Abstract:In this study, the synthesis of C f /(Hf 1/2 Zr 1/3 Ti 1/6 )C non-equimolar middle -entropy composites was reported through precursor infiltration and pyrolysis processing for the first time. The pyrolysis process of the (Hf 1/2 Zr 1/ 3 Ti 1/6 )C precursor was examined by XRD, while the resultant ceramic was characterized by SEM, EDS, and TEM. The results showed that precursor -derived (Hf 1/2 Zr 1/3 Ti 1/6 )C powders were characterized by single-phase and uniformly distributed elements from microscale to nanoscale. The C f /(Hf 1/2 Zr 1/3 Ti 1/6 )C composites exhibited a density of 2.741 g/cm 3 and a porosity of 11.49 vol%. The various elements were uniformly distributed throughout the material. It also demonstrated outstanding mechanical properties, with a flexural strength of 219.34 MPa and a modulus of 24.82 GPa. At the heat flux of 3 MW/m 2 , the oxides after ablation were inadequate to fully envelop the substrate. When the heat flux increased to 4 MW/m 2 , a dense Hf-Zr-Ti-O multiphase oxide layer was formed on the surface of the sample, providing the internal C f /(Hf 1/2 Zr 1/3 Ti 1/6 )C composites against further ablation. At the heat flux of 5 MW/m 2 , (Hf, Zr)TiO 4 was severely consumed. Our research expands the application scope of non-equimolar middle -entropy composites in the domain of ultra -high temperature ablation resistance.

Mechanical and Ablation Properties of a C/C-HfB2-SiC Composite Prepared by High-Solid-loading Slurry Impregnation Combined with Precursor Infiltration and Pyrolysis

Preparation, Ablation Behavior and Thermal Retardant Ability of C/C-HfB 2 -Sic Composites

Mechanical and ablation properties of 3D orthogonal woven C/C-SiC composite based on high-solid-loading slurry impregnation

Ablation Behavior of a C/C-ZrC-SiC Composite Based on High-Solid-loading Slurry Impregnation under Oxyacetylene Torch

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Preparation, Mechanical and Ablation Properties of a C/C-TaB2-SiC Composite

Ablative Property of C/C–SiC–HfC Composites Prepared Via Precursor Infiltration and Pyrolysis under 3,000 °C Oxyacetylene Torch

Ablation resistance of C/C-HfC composites

Ablation Resistance of HfC(Si, O)-HfB2(Si, O) Composites Fabricated by One-Step Reactive Spark Plasma Sintering

Ablation behavior of a three-dimensional C/C-HfC composite prepared by a precursor infiltration and pyrolysis method

Microstructure, Ablation Behavior and Thermal Retardant Ability of C/C-HfB2 Composites Prepared by Precursor Infiltration Pyrolysis Combined with Chemical Vapor Infiltration

Ablation of C/SiC-HfC Composite Prepared by Precursor Infiltration and Pyrolysis in Plasma Wind Tunnel

Ablation Properties of C/C-ZrC-SiC Composites

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Ablation Behaviour of C/C-HfC-SiC Composites Prepared by Joint Route of Precursor Infiltration and Pyrolysis and Gaseous Silicon Infiltration

Microstructure and Ablation Behavior of C/C–HfC Composites Prepared by Precursor Infiltration and Pyrolysis

Preparation and Ablation Properties of SiC Modified C/C Composites

Ablation Mechanism of Carbon/Carbon Composites Modified by HfC–SiC in Two Conditions under Oxyacetylene Torch

Ablation Performance of C/HfC-SiC Composites with In-Situ HfSi2/HfC/SiC Multi-Phase Coatings under 3000℃ Oxyacetylene Torch

Preparation and Ablation Behavior Analysis of Non-Equimolar C F /(hf 1/2 Zr 1/ 3 Ti 1/6 )C Composites under Oxyacetylene Flame with Different Heat Fluxes

Ablation Properties of HfB2 Coatings Prepared by Supersonic Atmospheric Plasma Spraying for SiC-coated Carbon/carbon Composites