Severe plastic deformation induced nano dispersion and strengthening effect in oxide dispersion strengthened copper fabricated by cold spray additive manufacturing
Yingbo Peng,Peiran Gao,Wei Zhang,Lang Cui,Shuyu Liu,Wenyu Chen,Jia Li,Rui Zhou,Guang Liu,Qihong Fang,Bin Liu
DOI: https://doi.org/10.1016/j.matchar.2023.113281
IF: 4.537
2023-08-31
Materials Characterization
Abstract:This work presented a novel net-shape-forming technology to prepare oxide dispersion strengthened (ODS) copper by cold spray additive manufacturing. There were three types of Al 2 O 3 particles in the internal oxidation Cu-Al 2 O 3 raw powders. After cold spraying, two types of nano-sized Al 2 O 3 inside the raw powder were inherited into the deposition, and the micro-sized Al 2 O 3 on the powder surface was crushed to nano-size under severe plastic deformation, which dispersed along the interface of deformed powder due to the plastic flow of Cu caused by adiabatic shearing. The plastic deformation produced by cold spraying was 20% higher than the hot extrusion with extrusion ratio of 11:1, which fully achieves the Al 2 O 3 fragmentation, dispersion distribution and densification of the cold sprayed deposition. Moreover, due to the significant work hardening and grain refinement effect by SPD during cold spraying, Vickers hardness and nanoindentation hardness of the ODS Cu deposition increased to 185.63 HV 3 and 2.76 GPa, respectively, which were significantly higher than the raw powders and hot extrusion sample.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing