Abstract:Wire arc additive manufacturing (WAAM) has high potential in fabricating large-scale structural components, offering advantages such as high forming efficiency, mold-free production, and superior energy utilization. Al-Cu alloys undergo rapid solidification and thermal cycling during WAAM, leading to anisotropy in their mechanical properties, which can compromise the performance of the alloys. To address this issue, this study proposes a homogenization treatment strategy. Employing electron microscopy, mechanical testing machines and other testing methods, a systematic analysis of the microstructure and mechanical properties of as-deposited Al-Cu alloys before and after homogenization is conducted. The investigation reveals that the as-deposited WAAM Al-Cu alloys exhibits a heterogeneous structure of fine equiaxed grains and coarse columnar grains, which significantly differentiates the mechanical properties along the scanning direction and the deposition direction. Notably, the elongation along the deposition direction falls below 8%, unsatisfactory for practical applications. An optimized homogenization treatment of 510°C for 24 hours is established. After homogenization, the coarse columnar grains transform into equiaxed grains, while the fine equiaxed grains grow, enhancing microstructural uniformity. Additionally, the homogenization treatment mitigates geometrically necessary dislocations and reduces solute segregation at grain boundaries. Consequently, the anisotropy in mechanical properties of WAAM Al-Cu alloys is eliminated after homogenization, and the elongation is elevated to over 10.2%. Moreover, we also found that homogenization facilitates the dissolution of coarse θ' phases and promotes the precipitation of θ″ phases during artificial aging, resulting in higher strength and ductility in T6 treated Al-Cu alloy.

Microstructure and properties research of Al-Zn-Mg-Cu alloy with high strength and high elongation fabricated by wire arc additive manufacturing

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

Al–Zn–Mg–Cu alloy with both high strength and high plasticity fabricated with wire arc additive manufacturing

Wire arc additive manufacturing of Al-Zn-Mg-Cu alloy: Microstructures and mechanical properties

Achieving high strength-ductility of Al-Zn-Mg-Cu alloys via hot-wire arc additive manufacturing enabled by strengthening precipitates

Insightful Investigation for the Strengthening Mechanisms of Al-Cu Alloy Prepared by Wire Arc Additive Manufacturing

Microstructure evolution and mechanical properties of Al–Cu–Mn–Cd alloy fabricated by CMT-wire arc additive manufacturing

Microstructure evolution and mechanical properties of wire-arc-additively manufactured Al–Cu–Mg–Ag alloy

Microstructures and Mechanical Properties of Al–Zn–Mg Aluminium Alloy Samples Produced by Wire + Arc Additive Manufacturing

Tensile, Fatigue Properties and Their Anisotropies of Al-Mg Alloy Fabricated by Wire-Arc Additive Manufacturing

Effect of Wire Composition on Microstructure and Properties of Wire and Arc Additive Manufactured ZAlCu5MnCdVA Aluminum Alloy

Microstructures and Properties of Al-Mg Alloys Manufactured by WAAM-CMT

Microstructure and mechanical properties of wire arc additively manufactured 205A high strength aluminum alloy: The comparison of as-deposited and T6 heat-treated samples

Microstructure evolution and mechanical properties of the wire + arc additive manufacturing Al-Cu alloy

Microstructure and mechanical properties of wire arc additive manufactured ZL205A alloy

Microstructure evolution and mechanical properties of the wire plus arc additive manufacturing Al-Cu alloy

Microstructure and Mechanical Properties of AlSi7Mg0.6 Aluminum Alloy Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT)

Microstructure and Mechanical Properties of Al-Cu-Mg Alloy Fabricated by Double-Wire CMT Arc Additive Manufacturing

Effects of Deposition Paramaters on the Microstructure Evolution of Wire Arc Additive Manufactured Al–Zn–Mg–Cu Alloy

Microstructure and mechanical properties of 600 MPa grade ultra-high strength aluminum alloy fabricated by wire-arc additive manufacturing

Microstructure and Mechanical Properties of Cu-6.5%Al Alloy Deposited by Wire Arc Additive Manufacturing