Abstract:Ultra-high strength 7xxx series aluminum alloys are widely used in aerospace applications due to their exceptional high specific strength. Wire + Arc Additive Manufacturing (WAAM) is a combination of arc and wire feeding additive manufacturing technology including either the gas tungsten arc (GTA) or the gas metal arc (GMA) process. And this technology has been applied in the aerospace manufacturing industry to reduce the time of product development and “buy-to-fly” ratios. However, the existing Al-Zn-Mg-Cu aluminum alloy filler wires are not suitable for WAAM process due to their high susceptibility to hot cracks. In this study, a novel Al-Zn-Mg-Cu-Sc aluminum alloy wire named 7A55-Sc with ultra-high strength and excellent hot-crack resistance has been successfully prepared by optimizing the composition of Al-Zn-Mg-Cu alloying elements and adding appropriate amounts of inoculants Sc and Zr elements during the smelting process. And then, thin-wall components without any hot cracks were successfully fabricated by using cold metal transfer (CMT) process. Results indicated that the microstructure of the as-deposited 7A55-Sc alloy consists of predominantly fine equiaxed grains and the average size of the grains is between 5.0 and 6.0 μm. The eutectics composed of α (Al), η phase and S phase were distributed along the grain boundaries. The Al3Sc and Al3 (Zr, Sc) particles precipitated within grains act as heterogeneous nucleation nuclei, promoting the formation of the equiaxed grains. After T6 heat treatment, most of the second phases distributed within grains and grain boundaries were dissolved into the α(Al) matrix. The distribution of alloy elements became more homogeneous. The average ultimate tensile strength, yield strength and elongation of T6 heat-treated 7A55-Sc alloy in the horizontal direction were 554 MPa, 488 MPa and 1.7% respectively, whereas 523 MPa, 469 MPa and 1.4% in the vertical direction. The lower ductility was considered due to the existence of a large number of pores in the 7A55-Sc alloy fabricated by the CMT process.

Wire and Arc Additive Manufacturing of High-Strength Al–Zn–Mg Aluminum Alloy

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

Wire arc additive manufacturing of Al-Zn-Mg-Cu alloy: Microstructures and mechanical properties

Microstructures and Properties of Al-Mg Alloys Manufactured by WAAM-CMT

Achieving high strength-ductility of Al-Zn-Mg-Cu alloys via hot-wire arc additive manufacturing enabled by strengthening precipitates

Microstructure and mechanical properties of ultra-high strength Al-Zn-Mg-Cu-Sc aluminum alloy fabricated by wire + arc additive manufacturing

Characterisation of a High-Performance Al–Zn–Mg–Cu Alloy Designed for Wire Arc Additive Manufacturing

Microstructure and Mechanical Properties of AlSi7Mg0.6 Aluminum Alloy Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT)

Characterisation of a High-Performance Al-Zn-Mg-Cu Alloy Designed for Wire Arc Additive Manufacturing

Microstructure and Mechanical Properties of Weaving Wire and Arc Additive Manufactured AZ91 Magnesium Alloy Based on Cold Metal Transfer Technique

Microstructure and mechanical properties of 600 MPa grade ultra-high strength aluminum alloy fabricated by wire-arc additive manufacturing

Microstructure and Mechanical Properties of Al-Cu-Mg Alloy Fabricated by Double-Wire CMT Arc Additive Manufacturing

Wire Arc Additive Manufacturing (WAAM) of Aluminum Alloy AlMg5Mn with Energy-Reduced Gas Metal Arc Welding (GMAW)

Microstructure evolution and mechanical properties of Al–Cu–Mn–Cd alloy fabricated by CMT-wire arc additive manufacturing

Microstructure and mechanical properties of wire arc additively manufactured 205A high strength aluminum alloy: The comparison of as-deposited and T6 heat-treated samples

Microstructure and properties research of Al-Zn-Mg-Cu alloy with high strength and high elongation fabricated by wire arc additive manufacturing

Large-size Ultra-High Strength-Plasticity Aluminum Alloys Fabricated by Wire Arc Additive Manufacturing Via Added Nanoparticles

The structure and mechanical properties of high-strength aluminum alloys fabricated with wire arc additive manufacturing

Arc Additively Manufactured 5356 Aluminum Alloy with Cable-Type Welding Wire: Microstructure and Mechanical Properties

Wire-arc additive manufacturing of AZ31 magnesium alloy fabricated by cold metal transfer heat source: Processing, microstructure, and mechanical behavior

Wire arc additive manufacturing of a novel ATZM31 Mg alloy: Microstructure evolution and mechanical properties