Insights from Raman spectroscopy of Diamond Deposition on Steel via Long-Term MPCVD

Clyde Varner II,Leslie Wilson

DOI: https://doi.org/10.26434/chemrxiv-2024-g808x

2024-07-13

Abstract:This research uses Raman spectroscopy to explore differences after Microwave Plasma Chemical Vapor Deposition (MPCVD) of diamond films on steel alloys (316L, 4140, and 1018) with a vanadium carbide interlayer to enhance adhesion and compatibility. The study reveals that a soft vanadium carbide interlayer and the FCC lattice match lead to a Ta-C film. The results of the graphite inhibition and diamond deposition varied with the steel alloy underlayer composition. In the 316L steel alloy, we successfully formed a thick, compressive strain-induced, sp3-bonded tetrahedral amorphous carbon layer without graphite. The findings have wide-ranging applications in environments demanding high durability and thermal conductivity.

Chemistry

What problem does this paper attempt to address?

This paper primarily investigates the deposition of diamond films on different types of steel alloys (316L, 4140, and 1018) using long-term microwave plasma chemical vapor deposition (MPCVD) method. Vanadium carbide (VC) interlayers were employed to improve the adhesion and compatibility between diamond and steel substrates. Through detailed analysis of Raman spectroscopy, the authors revealed the quality, phase composition, and defect structure of the diamond films.

The study found that 316L stainless steel, due to its low carbon content, alloying elements such as chromium, nickel, and molybdenum, and face-centered cubic (FCC) crystal structure, could form high-quality compressive strain-induced sp3-bonded tetrahedral amorphous carbon (ta-C) layers and successfully suppress graphite formation. In contrast, 1018 and 4140 steels, with their higher carbon content and other characteristics, were more favorable for diamond growth but exhibited a higher degree of graphitization.

The conclusion of the paper indicates that the unique combination of 316L stainless steel makes it an ideal substrate for depositing high-quality diamond films using MPCVD technology, which helps minimize graphite formation and enhance the quality of diamond coatings. These findings are significant for applications requiring high durability and thermal conductivity, such as electronics, energy storage, and nanotechnology, and provide a new perspective for materials science and technological innovation.