Abstract:In this master thesis, diamond-like carbon DLC/Cr bilayer systems, with thickness up to 1278 nm were formed on ABS, glass and Si substrates. Substrates surface were prepared by oxygen plasma cleaning process. The chromium thin film, which acts as a buffer layer, was grown by magnetron sputtering deposition. Diamond-like carbon was deposited by pulsed-DC PECVD, with methane and hydrogen as reactants. A Plackett-Burman experimental design was carried out in order to determine the influence of technological parameters of the deposition process on the thickness, deposition rate, intrinsic stress, contact angle, roughness, friction coefficient and wear rate of the obtained coatings. The independent variables were power, chamber pressure, time of deposition, total flux of the gases, composition of the reactant gases and oxygen plasma cleaning conditions. Values of intrinsic stress between 0.13-0.78 GPa were reported. Wear resistance measurements were performed by grinding calottes with a defined geometry. Low wear rate was achieved in the range of 1E-14 to 1E-15 m^3/Nm. The friction of the obtained coatings under different relative humidities, ranging 20 to 80% in a nitrogen environment, was measured using a nanotribometer with tungsten carbide ball. Results showed that friction coefficient increases with the increasing relativity humidity. Values from 0.12 to 0.24 for friction coefficient were reported. . The main objective of the DLC coating is to improve the wear resistance and tribological behavior of ABS in order to increase his durability for automotive, medical, household and textile applications, among others.

Diamond-Like Carbon Coatings on Plasma Nitrided M2 Steel: effect of deposition parameters on adhesion properties

Adhesion Enhancement on a Duplex DLC HiPIMS Positive Pulse Coating Performed by Active Screen Plasma Nitriding Pretreatment on 316L Stainless Steel Substrate

Tribological Behaviors of Diamond-Like Carbon Coatings on Plasma Nitrided Steel Using Three BN-containing Lubricants

The Formation of Diamond-Like Carbon Structure Anchored in the Nitrided Layer of M50 Steel During Plasma-Assisted Thermochemical Treatment

Diamond-Like Carbon Thin Films Deposited On Ti6al4v Alloy Surface By Plasma Gun At Atmospheric Pressure

On the adhesion of diamond‐like carbon coatings deposited by low‐pressure plasma on 316L stainless steel

Mechanical and Corrosion Study of Diamond-Like Carbon Coating on Niti Alloys

Effect of the DLC coating on the surface properties of the NiTi alloys

A study on the mechanical performance and medium temperature tribological behavior of plasma nitrocarburizing/TiAlSiN/DLC composite coating

Diamond-like Carbon Film on 20 CrNiMo Steel Prepared by Hollow-Cathode Glow Discharge

The Effects of Ti/Ni Doping on the Friction and Wear Properties of DLC Coatings

Experimental Study of Diamond-like Carbon Film on Aermet100 Steel and First-Principles Calculation of Interfacial Adhesion

Plackett-Burman experimental design for pulsed-DC-plasma deposition of DLC coatings

Deposition of DLC coating on biomedical TiNi alloys by plasma based ion implantation to improve surface properties

The Effect of DLC Surface Coatings on Microabrasive Wear of Ti-22Nb-6Zr Obtained by Powder Metallurgy

Improving Tribological Performance of Piston Ring Steel Substrates by DLC/Nano-crystalline Diamond Coating

Tribological study of lubricious DLC biocompatible coatings

Mechanical and Surface Characterization of Diamond-Like Carbon Coatings onto Polymeric Substrate

Excellent Adhered Thick Diamond-Like Carbon Coatings by Optimizing Hetero-Interfaces with Sequential Highly Energetic Cr and C Ion Treatment

Surface modification of NiTi alloys using diamond-like carbon (DLC) fabricated by plasma immersion ion implantation and deposition (PIIID)

Microstructure and Tribological Properties of Diamond-Like Carbon and Tialsicn Nanocomposite Coatings