Enhancing the Thermoelectric Performance of Cu2se Via Ag Doping

Shuaizhou Jiang,Meihua Hu,Shangsheng Li,Ying Tian,Di Liu,Haobo Zhang
DOI: https://doi.org/10.1016/j.jssc.2024.124951
IF: 3.3
2024-01-01
Journal of Solid State Chemistry
Abstract:Cu2Se as a thermoelectric material has gained popularity in recent years because of the excellent properties resulting from its superionicity. In this study, Cu2-xAgxSe (x = 0, 0.05, 0.15, 0.25) samples were fabricated through the spark plasma sintering method, followed by a comprehensive microstructure and thermoelectric properties analysis. The results indicated that, when the doping amount of Ag is x >= 0.05, the CuAgSe phase is produced at room temperature, which introduces an energy filtering effect, resulting in an augmentation of the Seebeck coefficient and a reduction in the electrical conductivity. Ag doping leads to point defects, the disorder of cations, and the phase boundaries which increases phonon scattering, resulting in reduced thermal conductivity. At 773 K, the thermal conductivity decreases from 1.10 Wm(-1)K(-1) for Cu2Se to 0.41 Wm(-1)K(-1) for Cu1.75Ag0.25Se. Compared to ZT similar to 0.8 for the intrinsic Cu2Se sample, the ZT of Cu1.75Ag0.25Se reaches 1.41 at 773 K, which is an increase of over 70 %.
What problem does this paper attempt to address?