Abstract:In this study, NiCrSiB-SiC composite coatings were prepared on 16Mn low-carbon steel by vacuum cladding technology using SiC and NiCrSiB mixed powders as raw materials for enhancing their wear resistance. The effects of different content of SiC particles on the microstructure evolution, mechanical and abrasive wear properties of the coatings were investigated. The results showed that SiC particles in all the NiCrSiB-SiC composite coatings with different SiC contents were completely decomposed into C and Si under the catalysis of Ni-based alloy. The out-diffused Si into the coating mainly led to the formation of the Ni 3 Si eutectic phase, while the out-diffused C introduced M 7 C 3 , M 3 C 2 , M 2 (C, B) and other hard phases. Besides, C also diffused to the substrate, leading to a carburizing effect, which remarkably enhanced the mechanical properties of the substrate. In the NiCrSiB-SiC composite coatings with high SiC content, the decomposition of SiC led to the remaining graphite phase. However, once the concentration of SiC was over high, excess graphite would deteriorate the compactness and adhesion of the coating, weakening its wear performance. The nanoindentation and abrasive wear experiments revealed that the composite coating with 5 wt% SiC particles had lower elastic modulus ( E ), higher hardness ( H ), H / E , and H 3 / E 2 , and its wear volume was only 1/10 of that of the substrate, indicating the best mechanical and wear properties. The excellent wear performance can be attributed to the combination of the in-situ formed carbides and borides hard reinforcing phases and the tough coating matrix composed of Fe and Si dissolved γ-Ni and Ni 3 Si eutectic phase.

Study on Tribological Performance of the Cocrni-Doped Sic Self-Lubricating Composites under Dry and Lubricated Conditions

A Novel CoCrNi-based Medium-Entropy Alloy Self-Lubricating Composite with Superior Wear Performance

Excellent Tribological Performance at Elevated Temperatures and Associated Mechanisms of Novel AlCoCrFeNi-MoS2 Solid Self-Lubricating Composite

Achieving Excellent Mechanical and Robust Lubrication Behavior in the CoCrNi Medium-Entropy Alloy Via In-Situ Graphite

An atomic insight into the stoichiometry effect on the tribological behaviors of CrCoNi medium-entropy alloy

Tribological behavior of NiCrW-based self-lubricating composites against IC10 alloy under high temperature and extremely slow sliding speed

Influence of Molybdenum Content and Load on the Tribological Behaviors of In-Situ Cr3C2-20 Wt % Ni Composites

Enhancement of Tribological Properties in Siliconized Graphite Via Hierarchically Hybrid SiC/C Composite

Development of Cu-15Ni-8Sn/MoS 2 self-lubricating composites with desirable mechanical and friction properties

Development of Cu-15Ni-8Sn/MoS2 Self-Lubricating Composites with Desirable Mechanical and Friction Properties

Microstructure evolution, mechanical and abrasive wear properties of NiCrSiB-SiC composite coatings prepared on 16Mn low-carbon steel by Ni-based alloy catalyzed SiC decomposition

Enhanced Mechanical and Tribological Capabilities of a Silicon Aluminum Alloy with an Electroplated Ni–Co–P/Si3N4 Composite Coating

Study of fabrication and wear properties of Ni–SiC composite coatings on A356 aluminum alloy

Preparation and Friction Properties of SiC-Al2O3/2A50 Co-Continuous Composites

3DN C/SiC Composites with Different Porosities for Tunable Lubrication Performance

Tribological Behavior of Ni–SiC Composite Coatings Produced by Circulating-Solution Electrodeposition Technique

Tribological Behavior of SiC Coating on C/C Composites Against SiC and WC under Unlubricated Sliding

Characterization and Wear Behaviors of Electrodeposited Ni-MoS2/SiC Composite Coating

Tribological Performance of Ni3Al–15 Wt% Ti3SiC2 Composites Against Al2O3, Si3N4 and WC-6Co from 25 to 800 °C

Tribological performance of Ti3SiC2 enhanced Ni3Al matrix composites

Influence of Ti 3SiC 2 content on tribological properties of NiAl matrix self-lubricating composites