Development of Cu-15Ni-8Sn/MoS2 Self-Lubricating Composites with Desirable Mechanical and Friction Properties

Ziyan Zhang,Yi Gao,Jinjuan Cheng,Xueping Gan,Chaoqiang Liu,Kechao Zhou

DOI: https://doi.org/10.1016/j.wear.2024.205428

IF: 4.695

2024-01-01

Wear

Abstract:This study focuses on the fabrication of Cu-based self-lubricating composites with desirable mechanical and friction properties using electroless plating and hot-pressing sintering and the analyses of the mechanical properties, friction properties and microstructures. High-strength Cu-15Ni-8Sn alloy and Cu-coated MoS2 prepared via electroless plating were selected to be the matrix and self-lubrication particles, respectively. A composite containing 20 vol.% Cu-coated MoS2 (C20) is developed, which has not only a desirable friction property but also a high mechanical property, e.g., transverse-rupture-strength of 433 MPa. The average friction coefficient and wear rate of C20 are 0.065 and 1.65 × 10-7 mm3/N·m, respectively, which are 13.3 % and 23.6 % lower than the composite containing 20 vol.% unmodified MoS2 (M20). The desirable mechanical property of C20 is attributed to the high-performance matrix, the good combination between the matrix and MoS2 particles and the uniform distribution of MoS2 particles in C20, and its good friction property owes to the formation of the solid lubricating film with a high adhesive strength during the wear process.