Development of Cu-15Ni-8Sn/MoS 2 self-lubricating composites with desirable mechanical and friction properties

Ziyan Zhang,Yi Gao,Jinjuan Cheng,Xueping Gan,Chaoqiang Liu,Kechao Zhou

DOI: https://doi.org/10.1016/j.wear.2024.205428

IF: 4.695

2024-05-31

Wear

Abstract:This study focuses on the fabrication of Cu-based self-lubricating composites with desirable mechanical and friction properties using electroless plating and hot-pressing sintering and the analyses of the mechanical properties, friction properties and microstructures. High-strength Cu-15Ni-8Sn alloy and Cu-coated MoS 2 prepared via electroless plating were selected to be the matrix and self-lubrication particles, respectively. A composite containing 20 vol.% Cu-coated MoS 2 (C20) is developed, which has not only a desirable friction property but also a high mechanical property, e.g., transverse-rupture-strength of 433 MPa. The average friction coefficient and wear rate of C20 are 0.065 and 1.65 × 10 -7 mm 3 /N·m, respectively, which are 13.3 % and 23.6 % lower than the composite containing 20 vol.% unmodified MoS 2 (M20). The desirable mechanical property of C20 is attributed to the high-performance matrix, the good combination between the matrix and MoS 2 particles and the uniform distribution of MoS 2 particles in C20, and its good friction property owes to the formation of the solid lubricating film with a high adhesive strength during the wear process.

materials science, multidisciplinary,engineering, mechanical