Tribological behavior and microstructural evolution of lubricating film of silver matrix self-lubricating nanocomposite

Xiao Kang,Shuang Yu,Hailin Yang,Yang Sun,Lei Zhang

DOI: https://doi.org/10.1007/s40544-020-0379-y

IF: 4.924

2020-11-09

Friction

Abstract:Abstract The aim of this study is to fabricate the nanocomposite with low friction and high wear resistance using binary solid lubricant particles. The microstructure and tribological performance of the nanocomposite are evaluated, and the composition and film thickness of the lubricating film are observed and analyzed by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The nanocomposite exhibited improved tribological properties with a friction coefficient as low as 0.12 and a low wear rate of 2.17 × 10 −6 mm 3 /(N·m) in high-purity nitrogen atmosphere. Decreasing sliding speed can increase lubricating film thickness, and the thickest lubricating film is approximately 125 nm. As the film thickness of the lubricating film exceeded 90 nm, the friction coefficient curves became smooth. In compared with WS 2 , MoS 2 can be more effective in forming the transfer layer on the worn surfaces at the initial stage of the tribological process.

engineering, mechanical

What problem does this paper attempt to address?

This paper aims to study the tribological behavior of silver - based self - lubricating nanocomposites and the microstructure evolution of the lubricating film. Specifically, the researchers prepared a silver - based self - lubricating nanocomposite containing binary solid lubricants (nano - scale WS₂ and micron - scale MoS₂) by hot - pressing sintering method. They evaluated the microstructure and tribological properties of this nanocomposite, and observed and analyzed the composition and thickness of the lubricating film by scanning electron microscope (SEM) and X - ray photoelectron spectroscopy (XPS).

The main objectives of the study include:
1. **Prepare nanocomposites with low friction and high wear resistance**: Use binary solid lubricant particles to prepare nanocomposites to improve their tribological properties.
2. **Evaluate the tribological properties of nanocomposites**: Test the friction coefficient and wear rate of nanocomposites at different sliding speeds through experiments.
3. **Analyze the microstructure of the lubricating film**: Use SEM and XPS techniques to observe and analyze the composition and thickness of the lubricating film, and explore the influence of the lubricating film on tribological properties.

Through these studies, the author hopes to reveal the formation mechanism of the lubricating film and its contribution to tribological properties, thereby providing theoretical basis and technical support for the development of high - performance self - lubricating materials.