Abstract:In recent years, the addition of Ni has been widely acknowledged to be capable of enhancing the mechanical properties of Al-Si alloys. However, the effect of Ni on the wear behaviors of Al-Si alloys and Al matrix composites, particularly at elevated temperatures, remains an understudied area. In this study, Al-Si-Cu-Mg-Ni/20wt% SiC particles (SiCp) composites with varying Ni contents were prepared by using a semisolid stir casting method. The effect of Ni content on the dry sliding wear behavior of the prepared composites was investigated through sliding tests at 25 and 350°C. Results indicated that the θ-Al 2 Cu phase gradually diminished and eventually disappeared as the Ni content increased from 0wt% to 3wt%. This change was accompanied by the formation and increase in δ-Al 3 CuNi and ε-Al 3 Ni phases in microstructures. The hardness and ultimate tensile strength of the as-cast composites improved, and the wear rates of the composites decreased from 5.29 × 10 −4 to 1.94 × 10 −4 mm 3 /(N·m) at 25°C and from 20.2 × 10 −4 to 7 × 10 −4 mm 3 /(N·m) at 350°C with the increase in Ni content from 0wt% to 2wt%. The enhancement in performance was due to the presence of strengthening network structures and additional Ni-containing phases in the composites. However, the wear rate of the 3Ni composite was approximately two times higher than that of the 2Ni composite due to the fracture and debonding of the ε-Al 3 Ni phase. Abrasive wear, delamination wear, and oxidation wear were the predominant wear mechanisms of the investigated composites at 25°C, whereas delamination wear and oxidation wear were dominant during sliding at 350°C.

Tribological Performance of Ni3Al–15 Wt% Ti3SiC2 Composites Against Al2O3, Si3N4 and WC-6Co from 25 to 800 °C

Tribological Behavior of Ni3Al Matrix Self-Lubricating Composites Containing WS2, Ag and Hbn Tested from Room Temperature to 800°C

Effect of Ti3SiC2 Content on Tribological Behavior of Ni3Al Matrix Self-Lubricating Composites from 25 to 800 °C

Tribological Behaviors of NiAl-Ti3SiC2Self-Lubricating Composites at Elevated Temperatures

Tribological performance of Ti3SiC2 enhanced Ni3Al matrix composites

Synergetic Lubricating Effect of WS2 and Ti3SiC2 on Tribological Properties of Ni3Al Matrix Composites at Elevated Temperatures

Tribological Performance Of Ni3al Self-Lubricating Composites With Different Content Of Tic At Elevated Temperature

Influence of Ti 3SiC 2 content on tribological properties of NiAl matrix self-lubricating composites

Tribological Behaviors of NiAl Based Self-Lubricating Composites Containing Different Solid Lubricants at Elevated Temperatures

Synergetic Lubricating Effect of MoS2 and Ti3SiC2 on Tribological Properties of NiAl Matrix Self-Lubricating Composites over a Wide Temperature Range

Excellent Tribological Performance at Elevated Temperatures and Associated Mechanisms of Novel AlCoCrFeNi-MoS2 Solid Self-Lubricating Composite

Wear and Friction of TiAl Matrix Self-Lubricating Composites against Si3N4 in Air at Room and Elevated Temperatures

Tribological properties of TiAl-Ti 3 SiC 2 composites

Effect of Ni content on the wear behavior of Al-Si-Cu-Mg-Ni/SiC particles composites

High-Temperature Tribological Performance of Ti 3 SiC 2 /tial Self-Lubricating Composite Against Si 3 N 4 in Air

Wear Properties of NiAl Based Materials

Tribological behavior of TiAl matrix self-lubricating composites containing silver from 25 to 800°C

Tribological behavior of NiCrW-based self-lubricating composites against IC10 alloy under high temperature and extremely slow sliding speed

Investigation on Microstructure and Wear Behavior of the NiAl–TiC–Al2O3 Composite Fabricated by Self-Propagation High-Temperature Synthesis with Extrusion

Investigation on Tribological Behavior of Ti2AlN/TiAl Composite at Room and Elevated Temperature

Effect of Sliding Speed and Applied Load on Dry Sliding Tribological Performance of TiAl Matrix Self-lubricating Composites