Abstract:TiAl matrix self-lubricating composites (TMC) with various weight percentages of Ti3SiC2 and MoS2 lubricants were prepared by spark plasma sintering (SPS). The dry sliding tribological behaviors of TMC against an Si3N4 ceramic ball at room temperature were investigated through the determination of friction coefficients and wear rates and the analysis of the morphologies and compositions of wear debris, worn surfaces of TMC, and the Si3N4 ceramic ball. The results indicated that TMC with 10wt% (Ti3SiC2-MoS2) lubricants had good tribological properties due to the unique stratification subsurface microstructure of the worn surface. The friction coefficient was about 0.57, and the wear rate was 4.22 x 10(-4) mm(3) (Nm)(-1). The main wear mechanisms of TMC with 10wt% (Ti3SiC2-MoS2) lubricants were abrasive wear, oxidation wear, and delamination of the friction layer. However, the main wear mechanisms of TMC without Ti3SiC2 and MoS2 lubricants were abrasive wear and oxidation wear. The continuous friction layer was not formed on the worn surfaces. The self-lubricating friction layer on the frictional surface, different phase compositions and hardness, as well as density of TMC contributed to the change in the friction coefficient and wear rate.

Wear and Friction of TiAl Matrix Self-Lubricating Composites against Si3N4 in Air at Room and Elevated Temperatures

High-Temperature Tribological Performance of Ti 3 SiC 2 /tial Self-Lubricating Composite Against Si 3 N 4 in Air

Synergetic Lubricating Effect of MoS2 and Ti3SiC2 on Tribological Properties of NiAl Matrix Self-Lubricating Composites over a Wide Temperature Range

Tribological Properties of TiAl Matrix Self-Lubricating Composites Containing Multilayer Graphene and Ti3SiC2at High Temperatures

Tribological Behaviors of NiAl-Ti3SiC2Self-Lubricating Composites at Elevated Temperatures

Tribological Performance Of Tial Matrix Self-Lubricating Composites Containing Ag, Ti3sic2 And Baf2/Caf2 Tested From Room Temperature To 600 Degrees C

Effect of Ti3SiC2 Content on Tribological Behavior of Ni3Al Matrix Self-Lubricating Composites from 25 to 800 °C

Tribological Behaviors of NiAl Based Self-Lubricating Composites Containing Different Solid Lubricants at Elevated Temperatures

Tribological behavior of TiAl matrix self-lubricating composites containing silver from 25 to 800°C

Excellent Tribological Performance at Elevated Temperatures and Associated Mechanisms of Novel AlCoCrFeNi-MoS2 Solid Self-Lubricating Composite

Tribological properties of TiAl-Ti 3 SiC 2 composites

Effect of Ag and Ti3SiC2 on Tribological Properties of TiAl Matrix Self-lubricating Composites at Room and Increased Temperatures

Friction and Wear Properties of TiAl-Ti3SiC2-MoS2 Composites Prepared by Spark Plasma Sintering

Tribological Performance Of Ni3al Self-Lubricating Composites With Different Content Of Tic At Elevated Temperature

Effect of Sliding Speed and Applied Load on Dry Sliding Tribological Performance of TiAl Matrix Self-lubricating Composites

Dry Sliding Wear of TiAl-Graphene-Silver Composite at Elevated Temperatures

Synergetic Lubricating Effect of WS2 and Ti3SiC2 on Tribological Properties of Ni3Al Matrix Composites at Elevated Temperatures

Tribological Behavior of Ni3Al Matrix Self-Lubricating Composites Containing WS2, Ag and Hbn Tested from Room Temperature to 800°C

Tribological Performance of Ni3Al–15 Wt% Ti3SiC2 Composites Against Al2O3, Si3N4 and WC-6Co from 25 to 800 °C

Effect of Temperature on Tribological Properties of Tial Based Self-Lubricating Composites

Investigation on Tribological Behavior of Ti2AlN/TiAl Composite at Room and Elevated Temperature