Abstract:The Cr2AlC ternary ceramic compound, which belongs to the MAX phase family, has unique properties, such as high temperature strength, oxidation and corrosion resistance, good electrical and thermal conductivity, and machinability. It has been demonstrated that crack damage in this type of ceramics can be repaired by selective oxidation of the aluminium atoms. The alumina formed in the crack gap has a strong adhesion to the fracture surfaces enabling full strength recovery. However, it was observed that the restoration of the properties upon exposure to high temperature air is very slow, most likely to be due to the slow supply of Al atoms. Given the importance of grain boundaries as a path for rapid element supply to the fracture surface, it is to be expected that the strength and healing efficiency depend on the grain size of the MAX phase material. But this relation has not been demonstrated yet. It is therefore interesting to study the effect of grain size on the oxidation induced crack healing of Cr2AlC. In our work, the Cr2AlC ceramics are produced by reactive hot-press sintering using the chromium, aluminum and graphite powders as the starting materials. The grain size of Cr2AlC ceramics was controlled by adjusting the sintering temperature and holding time. In this way several materials with an average grain size in the range of 10 to 50 μm were obtained. X-ray diffraction was used to verify the phase compositions of Cr2AlC ceramics. Crack damage was induced with a Knoop indentator in three point bending samples The flexural strength and fracture toughness of the initial material before and after healing were determined by three point bending tests and the single edge notch beam technique, respectively. The precracked specimens were healed at 1100 °C in air for various times. From the experimental data the strength recovery was determined as a function of the Cr2AlC grain size and the observations are used to build a general model for crack healing in MAX phase materials ICSHM2013 _________________________________________________________________________________

Influence of Cr2AlC on the Thermal Shock and Corrosion Resistance of Low Carbon Al2O3-C Refractory

Enhanced thermal shock resistance of low-carbon Al2O3-C refractories with direct CVD synthesis of nano carbon decorated oxides

Effects of Cr2O3 Content on Microstructure and Mechanical Properties of Al2O3 Matrix Composites

The influence of nanoparticles and functional metallic additions on the thermal shock resistance of carbon bonded alumina refractories

Enhanced thermal shock resistance of low‐carbon Al2O3‐C refractories via CNTs/MgAl2O4 whiskers composite reinforcement

Nanoscale toughening of low carbon Al2O3‐C refractories by means of SiCnw/Al2O3 composite reinforcement

Synergic Effects of Nano Carbon Sources on Thermal Shock Resistance of Al2O3-C Refractories

High-temperature performance in Al2O3–Cr2O3 refractories: Effect of Al2TiO5

Improved thermal shock resistance of low-carbon Al2O3–C refractories fabricated with C/MgAl2O4 composite powders

Microstructure evolution of Cr 2 AlC MAX phase under a graphite bed between 1100 °C and 1500 °C

Effect of Zircon, B4C and Coke Additions on Oxidation Resistance Properties of Al2O3-C Refractories

Microstructure, phase evolution, mechanical properties and slag corrosion resistance of ZrO2 reinforced Al2O3–Cr2O3 composites

Enhanced oxidation resistance and thermal shock resistance of low-carbon Al 2 O 3 –C refractories with nano-BN: A synergistic of mullitization behavior

Effect of annealing on the microstructure, mechanical and electrochemical properties of CrAlC coatings

Phase composition, microstructure, and properties of Al4O4C–(Al2OC)1-(AlN) –Zr2Al3C4–Al2O3 refractories prepared at high temperatures in nitrogen

Molten salt synthesis of Cr3C2-coated flake graphite and its effect on the physical properties of low-carbon MgO–C refractories

Enhancing the thermal shock and corrosion resistance of low‐carbon Al2O3–C refractories: The role of h‐BN composite powder

Enhanced performance of low-carbon MgO–C refractories with nano-sized ZrO2–Al2O3 composite powder

Inhibition of Cr6+ in calcium aluminate cement bonded refractory castables using chrome-hibonite, Ca(Al,Cr)12O19 raw materials

The Effect of Grain Size on the Mechanical Properties and the Oxidation Induced Crack Healing Efficiency of CR2ALC Ceramic

High-Temperature Chemical Stability of Cr(III) Oxide Refractories in the Presence of Calcium Aluminate Cement