Abstract:Magnesia-chrome refractories have been essential materials for application as wear lining in copper production furnaces for many years. Formation of hexavalent chromium (Cr(VI)) has been a major concern despite its admirable corrosion resistance in copper slag. Magnesia-chrome refractory specimens (9, 12, 15 and 18 wt% Cr2O3) with addition of Al2O3 and TiO2 were fabricated and subsequent corrosion tests using copper slag was conducted in air. The corrosion mechanism between magnesia-chrome refractories fabricated and synthetic copper slag were investigated by means of X-ray diffraction (XRD) and scanning electron microscope (SEM), and concurrent formations of Cr(VI) were assessed effectively by leaching test. All the magnesia-chrome specimens prepared are composed of periclase and composite spinel Mg(Al,Cr,Ti)(2)O-4 phases after firing at 1700 degrees C. Densification of the specimens decreases with the increase in Cr2O3 content due to the increased volume expansion, while TiO2 addition can improve their densification as mass transfer is enhanced during the sintering process. The corrosion resistance of the specimens decreases slightly with the Cr2O3 content due to the increased apparent porosity, which would result in penetration of more corrosive slag at the initial stage of the corrosion test while a newly formed (Mg,Cu)(Cr,Fe)(2)O-4 spinel dense layer between the slag and penetration layer effectively hinders further penetration of slag and well protects the specimens. The Cr(VI) in the specimens prepared increases obviously with the Cr2O3 added content, while the TiO2 addition can suppress the formation of Cr(VI) effectively and the copper slag can cause the formed Cr(VI) to be reduced further during the corrosion process. For all the specimens, concentrations of Cr(VI) in the leachates is much lower than the US-EPA limit of 100 mg/kg but exceeds the European limit of 2 mg/kg after the corrosion test. (C) 2019 Elsevier B.V. All rights reserved.

Inhibition of Cr6+ in calcium aluminate cement bonded refractory castables using chrome-hibonite, Ca(Al,Cr)12O19 raw materials

High-Temperature Chemical Stability of Cr(III) Oxide Refractories in the Presence of Calcium Aluminate Cement

Leaching kinetics of Cr(VI) phases in the matrices of calcium aluminate cement-bonded refractory castables: Role of micro-silica

Inhibited Cr(VI) formation in Cr2O3-containing refractory castable using reactive MgO as hydraulic binder

Effects of Alkali on Water Soluble Hexavalent Chromium in Ordinary Portland Cement

Inhibition of Cr6+ by the formation of in-situ Cr3+ containing solid-solution in Al2O3–CaO–Cr2O3–SiO2 system

Enhancing mechanism of improved slag resistance of Al2O3-spinel castables added with pre-synthesized (Al,Cr)2O3 micro-powder

Formation Mechanisms and Leachability of Hexavalent Chromium in Cr2O3-Containing Refractory Castables of Electric Arc Furnace Cover

Corrosion mechanism of cement-bonded Al2O3–MgAl2O4 pre-cast castables in contact with molten steel and slag

High-temperature stability and leaching kinetics of the hexavalent chromium compound, chrome-hauyne (Ca4Al6CrO16)

Corrosion Mechanisms of Magnesia-Chrome Refractories in Copper Slag and Concurrent Formation of Hexavalent Chromium

Effects of Cr2O3 Content on Microstructure and Mechanical Properties of Al2O3 Matrix Composites

Preparation of CaCO3 coated corundum aggregates by dip-coating and heat treatment and its effects on the properties and microstructures of Al2O3–MgO castables

Effect of Calcium Oxide on Chromium Solidification During the Melting of Hazardous Waste Incineration Fly Ash.

High-temperature performance in Al2O3–Cr2O3 refractories: Effect of Al2TiO5

Effect of oxide interactions on chromium speciation transformation during simulated municipal solid waste incineration

Influence of bonding systems on the properties of Al 2 O 3 -MgO refractory castables: Aluminate cement and alumina silica gel

Restructuring-diffusion mechanism of calcium alumino-titanate in CaAl12O19–MgAl2O4–Al2O3 castables

Feasibility of using Cr-containing vitrification product as cement admixture: Structural evolution and chromium immobilization

Understanding of leaching, immobilization and oxidation behaviors of chromium in Cr 2 O 3 -doped aluminosilicate glasses

Corrosion mechanism of reactive MgO‐bonded Cr2O3‐bearing castables in CaO–Al2O3–Fe2O3–SiO2‐based steel‐making slag