Abstract:The composition modification by the inclusion of Li2O, Na2O, K2O, and GeO2 in barium–zinc–CA glasses can limit the excess oxygen defect formation with their charge compensator or glass former role. Highly diffusive Li and Na‐glasses reduce the O3− centers, whereas those are promoted in K‐glasses compared to base glass. However, GeO2 addition reduces all the defects significantly. This is further confirmed by optical probing with Cr ions that displays broadband near‐infrared emission in selected glasses. Calcium aluminate (CA)‐based glasses have drawn significant attention owing to their pronounced optical, mechanical, and chemical properties for potential applications in IR photonics. Nonetheless, limitations related to their poor glass‐forming ability was addressed by incorporating ZnO that has formed negatively charged [ZnO4]2− and [AlO4]− units, thereby generating the oxygen‐excess defects. These defects impart a detrimental effect on the optical properties. Thus, the present study explores the impact of Li2O, Na2O, K2O, and GeO2 inclusion in the barium–zinc–calcium–aluminate (BZCA) glass to eliminate the oxygen‐excess defects. The molecular structure of the glass matrix was examined by Raman, NMR, and XPS along with the bulk diffusivity of the glasses through MD simulation and are correlated to elucidate the origin of the defect centers. Due to higher diffusivity, Li+ and Na+ cations decrease Al–O hole centers (Al–OHC) and O3− defects but promote F+ (Farbe) centers while K+ ions having lower diffusivity and enhance the O3− defects. Interestingly, all the defect centers are substantially reduced in GeO2‐containing glasses. Further, multivalent Cr ions are doped to optically probe the defect centers through UV–Vis–NIR absorption and photoluminescence spectra. Cr3+ and Cr4+ are found dominant in Li+‐and Na+‐containing glasses due to the presence of less O3− defect, whereas excess O3− converts all Cr3+ into Cr6+ for K+‐containing glasses. Additionally, broadband NIR emission from Cr4+ can functionalize selective glasses for laser and telecommunication applications.

Improving the UV Transmittance of Synthetic Quartz Through Defect Repair Methods

Generation and Recombination of Defects in Vitreous Silica Induced by Irradiation with a Near-Infrared Femtosecond Laser

Tuning the peak position of subwavelength silica nanosphere broadband antireflection coatings.

Fabrication and Visible Emissions of ZnO Nanocrystal Doped Transparent Zinc Silicate Glass-Ceramics

Combined non-destructive evaluation of the damage precursors in fused silica optics

Defects and solarization in YAG transparent ceramics

Growth of Diamond Thin Films with Smooth Surface and High Transmittance on Quartz Glass Substrates

Investigations on the Photoluminescence Spectra and Its Defect-Related Nature for the Ultraviolet Transmitting Fluoride-Containing Phosphate-Based Glasses

The transformation balance between two types of structural defects in silica glass in ion-irradiation processes

A New Insight into the Influence of Fluid Inclusions in High-Purity Quartz Sand on the Bubble Defects in Quartz Glass: A Case Study from Vein Quartz in the Dabie Mountain

Strong UV laser absorption source near 355 nm in fused silica and its origination

Effect of Different Etching Processes on Surface Defects of Quartz Crystals

Research on the mitigation of redeposition defects on the fused silica surface during wet etching process

Surface and Subsurface Damage of Fused Quartz Glass Induced by Shear-Thickening Polishing

Defect Engineering of Nanocrystal‐In‐Glass Composites for Ultrashort Optical Pulse Monitoring

Improving Optical Efficiency and Durability With Solid–Liquid Mixed Gels in Ultraviolet Light-Emitting Diodes

Mechanisms for low-temperature direct bonding of Si/Si and quartz/quartz via VUV/O3 activation

Defect center–tailored calcium aluminate glasses for photonic applications: Unveiling structure–diffusivity correlation

Femtosecond Laser Induced Defects in Various Silica Glasses

Advanced Processing Techniques and Impurity Management for High-Purity Quartz in Diverse Industrial Applications

Suppression of Defect-Induced Quenching Via Chemical Potential Tuning: A Theoretical Solution for Enhancing Lanthanide Luminescence