Abstract:Microstructures, textures, mechanical properties and fracture behaviors of a newly developed near alpha titanium alloy were investigated systematically at room temperature (RT) and high temperatures (600 degrees C and 650 degrees C). Microstructure observations revealed that alpha colonies with large size in as-casted alloy were either broken into deformed alpha lamellas or colonies with small size, or transformed into equiaxed alpha grains by recrystallization. The recrystallized equiaxed structure exhibited lower texture intensities and poor preferential crystallographic orientation comparing with macro-zones corresponding to deformed alpha colonies. And recrystallized structure played an important role in reducing texture intensities of overall alpha phase. Due to more recrystallized equiaxed alpha grains, the maximum texture intensity of 980E-A was slightly lower than that of 980E-B. Moreover, TEM analyses proved that silicides promoted the recrystallization of alpha grains by pinning dislocations during forging. Comparison between current alloys with commonly used near alpha titanium alloys indicated that 980E-A exhibited optimal combination of mechanical properties at RT and 600 degrees C. Observations of fracture surfaces found that silicides played an important role in the formation of voids and dimples due to the production of inhomogeneous plastic deformation and stress concentration around them. Meanwhile, silicides displayed stress bearing effect during tensile process. By observations of longitudinal section, voids closing to fracture surface were mainly located in two types of areas. First type of areas was the vicinity of macro-zones. Second type mainly distributed at the edges of coarse grain areas. Boundaries of lamellar alpha grains in a single deformed alpha colony were also the preferential formation sites of voids and micro-cracks.

Influences of Microstructures and Macrozones on the Stress Corrosion Cracking Sensitivity of a Near Alpha Titanium Alloy

Deformation in Fatigue Crack Tip Plastic Zone and Its Role in Crack Propagation of Titanium Alloy with Tri-Modal Microstructure

Influence of macrozones on the fatigue cracking behavior and fracture mechanisms of rolled Ti–6Al–4V alloy

Microstructural evolution, mechanical properties and fracture toughness of near β titanium alloy during different solution plus aging heat treatments

Investigation of Microstructures, Textures, Mechanical Properties and Fracture Behaviors of a Newly Developed Near Α Titanium Alloy

Characterization Of Microstructural Evolution For A Near-Alpha Titanium Alloy With Different Initial Lamellar Microstructures

Microstructural Influences on the High Cycle Fatigue Life Dispersion and Damage Mechanism in a Metastable Β Titanium Alloy

Fatigue Crack Growth Behavior of Beta-Annealed Ti–6Al–2Sn–4Zr–xMo (x = 2, 4 and 6) Alloys: Influence of Microstructure and Stress Ratio

Effect of Microstructure on the Fatigue Crack Propagation Behavior of Tc4-Dt Titanium Alloy

Deciphering the Role of Macrozones in the Microstructure Globularization and Tensile Fracture: Insights from a New Developed Marine Engineering Titanium Alloy

Influence of microstructure on tensile strength and fracture toughness of a Ti-13Nb-13Zr alloy

Nanoscale perspective on the stress-corrosion cracking behavior of a peak-aged 7XXX-Al alloy

Plane Strain Fracture Behavior of a New High Strength Ti–5Al–3Mo–3V–2Zr–2Cr–1Nb–1Fe Alloy During Heat Treatment

Ex-situ study on mechanical properties and deformation mechanism of three typical microstructures in TA19 titanium alloy

Effect of Grain Structure on the Stress Corrosion Cracking (SCC) Behavior of an As-Extruded Mg-Zn-Zr Alloy

The effects of grain morphology and crystallographic orientation on fatigue crack initiation in a metastable titanium alloy Ti-7333

Investigation of the Influence of Macrozones in Titanium Alloys on the Propagation and Scattering of Ultrasound

The Effect of Microstructure on the Mechanical Properties of TC4-DT Titanium Alloys

Study on Fatigue Behavior and Fracture Mechanism of LMD Ti-6.5Al-3.5Mo-1.5Zr-0.3Si Alloy Based on Microstructure

Influence of Alloyed Sc and Zr, and Heat Treatment on Microstructures and Stress Corrosion Cracking of Al–Zn–Mg–Cu Alloys

Microstructural morphology effects on fracture toughness and crack growth behaviors in a high strength titanium alloy