Effect of cooling rate during annealing on microstructure and ultrasonic cavitation behaviors of Ti6Al4V alloy

Yijing Wang,Yulong An,Guoliang Hou,Xiaoqin Zhao,Huidi Zhou,Jianmin Chen

DOI: https://doi.org/10.1016/j.wear.2022.204529

IF: 4.695

2023-01-15

Wear

Abstract:Crack propagation is one of the most important failure modes in cavitation erosion, which is microstructurally-sensitive. Thus, the microstructure of Ti6Al4V alloy was regulated by annealing with different cooling rates to investigate its cavitation erosion resistance in this study. The effect of microstructure evolution of Ti6Al4V alloy on its crack propagation behavior under ultrasonic cavitation was discussed in detail. The results showed that cracks firstly initiated at the interface between α/β phase and then extended to β phase surface under the impact of ultrasonic cavitation. Because of the existence of fewer slip systems, higher hardness and elastic resilience of α phase, as well as the existence of substructures inside of α phase, it was difficult to initiate and propagate cracks in α phase of Ti6Al4V alloy than β phase during cavitation erosion. Besides, the Ti6Al4V alloy after heat treatment with air cooling showed excellent cavitation erosion resistance. The reason came from two aspects that acicular secondary α grains precipitated inside of transformed β (βT) phase and nanotwins formed in the interface between βT phase and primary α phase, resulting in the better crack propagation resistance of Ti6Al4V alloy after heat treatment with air cooling.

engineering, mechanical,materials science, multidisciplinary