Abstract:The aim of this work is to investigate the effect of heat treatment (T6) on the microstructure, mechanical, and corrosion properties of Al 319.0 alloy. In particular, Al 319.0 alloy is developed by squeeze casting using 200 MPa pressure, and further the ingots are solutionized, quenched and artificially aged to develop a homogenous microstructure, improve distribution of secondary phase(s), and mechanical properties at ambient and elevated temperatures. The phase and microstructure of the as-cast and heat-treated Al 319.0 alloys analyzed using X-ray diffraction, optical microscope, and field emission scanning electron microscope illustrate cast ingot contain α -Al as a primary phase and Al 2 Cu, eutectic Si, and Al 5 Si 7 Cu-containing intermetallic as secondary phase(s). However, heat treatment leads to complete dissolution of Al 5 Si 7 Cu and partial dissolution and re-precipitation of Al 2 Cu phase. Moreover, heat treatment changes the morphology of eutectic Si into spheroidal Si, blocky Al 2 Cu into spheroids Al 2 Cu, and the heat-resistant α (FeMn), Al 8 Cu 3 Mn(Si) phases emerged. The tensile test at room and elevated temperatures exhibit significant improvement in the YS and UTS at ambient temperature in heat-treated alloy owing to the presence of precipitation-hardened phases. Importantly, these phases are found stable up to 150 °C and tend to coarsen at 250 °C owing to thermal softening invariably leading to a substantial reduction in mechanical properties. Potentiodynamic polarization and electrochemical impedance spectroscopy shed light on galvanic corrosion phenomena predominant in 0.1 M NaCl solution. In particular, heat-treated alloy specimens demonstrated the lowest corrosion current ( I corr —~1.72 μA/cm 2 ) , and highest polarization resistance ( R p —12260 Ω.cm 2 ) implying superior corrosion resistance as compared to as-cast alloy owing to protective barrier provided by finer Al 2 Cu precipitates and spheroidal Si.

Effect of heat treatment on corrosion and ultrasonic cavitation erosion resistance of AlSi10MnMg alloy

The Effect of Heat Treatment on the Mechanical Properties and Oxidation Resistance of AlSi10Mg Alloy

Effect of Solution Heat Treatment on Microstructure and some Properties of Al–Cu–Mg Alloy

The Influence of Heat Aging Treatments on the Cavitation Erosion Behavior of a Type 6082 Aluminum Alloy

Effect of solution heat treatment on the internal architecture and compressive strength of an AlMg4.7Si8 alloy

Study on microstructure and properties of Mg-Al-Si-Ca alloy by heat treatment

Effect of heat treatment on the microstructure and mechanical properties of Al‐9Si‐0.4Mg‐0.1Cu alloy

Effect of heat treatments on microstructure and mechanical properties of sand cast Al–2Li–2Cu–0.5Mg–0.2Sc–0.2Zr alloy

Effect of chemical composition and T6 heat treatment on microstructure and mechanical properties of a hyper eutectic Al–Si alloy

Effect of Heat Treatment on the Microstructures and Mechanical Properties of Al–4Cu–1.5Mg Alloy

Effect of Heat Treatment on Microstructure, Mechanical, and Corrosion Properties of Squeeze Cast Al 319.0 Alloy

Microstructure Evolution of Modified Die-Cast AlSi10MnMg Alloy During Solution Treatment and Its Effect on Mechanical Properties

Effect of Solution and Aging Treatment on Microstructure and Mechanical Properties of Al–14Si–5Cu–1.1Mg–2.3Ni–0.3La Alloy

Effects of Adding Trace Modification Elements and Heat Treatment on the Strength and Toughness of AlSi8Cu2MgMn Alloy

Correlation between Mechanical Properties—Structural Characteristics and Cavitation Resistance of Cast Aluminum Alloy Type 5083

Microstructure and Mechanical Properties of Cast Al-Si-Cu-Mg-Ni-Cr Alloys: Effects of Time and Temperature on Two-Stage Solution Treatment and Ageing

Effect of cooling rates and heat treatment time on Si phase of AlSi10Mg alloy manufactured by selective laser melting: Microstructure evolution and strengthening mechanism

Effects of Heat Treatment on Microstructure and Mechanical Properties of AlSi10Mg Fabricated by Selective Laser Melting Process

Microstructure evolution and mechanical behavior of Cu-7Ni-7Al-4Fe-2Mn alloy via a quenching-aging heat treatment

Influence of the Solution and Artificial Aging Treatments on the Microstructure and Mechanical Properties of Die-Cast Al–Si–Mg Alloys

Effect of heat treatment on microstructure and mechanical properties of Cu–6.9Ni–2.97Al–0.99Fe–1.06Mn alloy