Abstract:Lead zirconate titanate (PZT) ceramics were prepared by direct coagulation casting via high valence counterions (DCC–HVCI) using magnesium citrate as a coagulating agent assisted by the hydrolysis of glycerol diacetate. The colloidal behavior of PZT suspensions was evaluated by measuring the zeta potential and the viscosity. The dispersant content and solid loading were optimized to prepare concentrated PZT suspension. The results indicated that PZT suspension with solid loading up to 56vol% can be prepared by the addition of 0.5wt% ammonium polyacrylate at pH=10.6. The critical coagulation concentrations of magnesium and lead in 56vol% PZT suspensions are 15 and 35mM, respectively. The viscosity of 56vol% PZT suspensions with 0.5–1.0wt% magnesium citrate and 2vol% glycerol diacetate is higher than 30Pas at 60°C for 30min which is sufficient to coagulate the suspensions. The coagulating time is 60–90min at 50–70°C. The compressive strength of the coagulated wet samples decreases with the increase of coagulating temperature, but increases with the increase of magnesium citrate content. The strength is in the range 1.5–2.8MPa which is sufficiently high for demolding and handling without deformation. Dense PZT ceramics sintered at 1250–1280°C show homogeneous microstructures with relative densities of 99.2–99.7% and good piezoelectric properties compared with a traditional die pressing method.

Flash Sintering of Lead Zirconate Titanate Ceramics under High Voltage at Room Temperature

Low‐Temperature Sintering of Lead‐Based Piezoelectric Ceramics

Rapid sintering of lead zirconate titanate ceramics at low temperature by spark plasma sintering

Flash Sintering of ZnO Ceramics with Combined Power Supplies at Room Temperature

Flash Sintering of ZnO Ceramics at Room Temperature with Bisectional Electrode Distributions

Gas-discharge induced flash sintering of YSZ ceramics at room temperature

Enhancing Electrical Properties of High-Curie Temperature Piezoelectric Ceramics BNT-PZT and Their Mechanism

Low-Temperature Sintering of Pzt Ceramics

Low-Temperature Sintering of Lead Magnesium Nickel Niobate Zirconate Titanate (Pmn-Pnn-pzt) Piezoelectric Ceramic, with High Performances

Microstructure and piezoelectric properties of PMS–PZT ceramics

Influence of Spark Plasma Sintering Temperature on Piezoelectric Properties of PZT-PMnN Piezoelectric Ceramics

Novel liquid–phase flash sintering of lead zirconate titanate piezo‐ceramics

Alternating Current Field Flash Sintering 99% Relative Density ZnO Ceramics at Room Temperature

Facile Preparation and Performance of Novel High-Tc Xbi(ni1/2ti1/2)o3-(1-x)pb(zr1/2ti1/2)o3 Piezoceramics

Optimizing structure and electrical properties of high-Curie temperature PMN-PHT piezoelectric ceramics via tailoring sintering process

Microstructures And Pyroelectric Properties Of Multicomposition 0.9pbzro(3)Center Dot Xpbtio(3)Center Dot(0.1-X)Pb(Zn1/3nb2/3)O-3 Ceramics

Effect of atmospheric conditions on the onset electric field of ZnO and Y2O3 ceramics flash sintering at room temperature

Effect of atmospheric conditions on the onset electric field of ZnO and Y<sub>2</sub>O<sub>3</sub> ceramics flash sintering at room temperature

High Piezoelectric D33 Coefficient of Lead-Free (ba0.93ca0.07)(ti0.95zr0.05)o3 Ceramics Sintered at Optimal Temperature

Microstructures and Pyroelectric Properties of Multicomposition 0.9PbZrO<sub>3</sub>·<i>x</i>PbTiO<sub>3</sub>·(0.1−<i>x</i>)Pb(Zn<sub>1/3</sub>Nb<sub>2/3</sub>)O<sub>3</sub>Ceramics

Enhanced Piezoelectric Properties of PZT Ceramics Prepared by Direct Coagulation Casting Via High Valence Counterions (DCC–HVCI)