Introducing nano-scale MgO particles into RHQT Nb 3 Al superconducting wires to significantly improve the critical current density

Changkun Yang,Guangbin Liu,Yuyao Zhang,Shulong Li,Xiaguang Sun,Min Xu,Lian Liu,Yongliang Chen,Wentao Wang,Yong Zhang,Yong Feng,Zhou Yu,Yong Zhao

DOI: https://doi.org/10.1016/j.jallcom.2023.172452

IF: 6.2

2023-10-09

Journal of Alloys and Compounds

Abstract:This research introduced nano-scale particles into the RHQT Nb 3 Al superconducting wires, which was confirmed by TEM that nanoparticles with size of 5-25 nm distributed in the wires and might act as the extra flux pinning centers. The precursor wires were fabricated by powder in tube process with nano-sized MgO (n-MgO) doped in the raw powder. Uniform microstructure and chemical composition were obtained in the superconducting wires. Besides nanoparticles, high density stacking faults with spacing of 5-20 nm were observed in the Nb 3 Al superconducting wire, which acted as the dominant flux pinning centers. It had great importance that nanoparticles were introduced into the RHQT Nb 3 Al wires and combined with the high density stacking faults to significantly improve the critical current density ( J c ) of the wires. The magnetic J c results of 1 wt.% n-MgO doped Nb 3 Al wire were about twice of the non-doped sample, corresponding to J c values of 3.18×10 5 A/cm 2 , 2.38×10 5 A/cm 2 and 1.72×10 5 A/cm 2 at 4.2 K and 8 T, 10 T and 12 T.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering