Brazing temperature and time effects on the mechanical properties of TiC cermet/Ag–Cu–Zn/steel joints
L.X. Zhang,J.C. Feng,P. He
DOI: https://doi.org/10.1016/j.msea.2005.11.044
2006-01-01
Abstract:This study investigates the influences of brazing temperature and time on mechanical properties of TiC cermet/Ag–54Cu–33Zn/steel joint. Test result shows that interface products of the brazed joint are, respectively (Cu, Ni), Ag (s.s)+Cu (s.s), (Cu, Ni), (Cu, Ni)+(Fe, Ni) from TiC cermet to steel side. When the brazing temperature is low or time is short, the joint belongs to cleavage and quasi-cleavage fracture and the fracture site is on the interface of (Cu, Ni)/Ag (s.s)+Cu (s.s). When the brazing temperature and time are increased to 850°C and 15min, the joint achieves the maximum shear strength 95.7MPa, which is tough and cleavage fracture and the major fracture site is in Ag (s.s)+Cu (s.s) zone. Furthermore, when the brazing temperature or time continues to be increased, the joint belongs to cleavage and quasi-cleavage fracture and the joint cracks in (Cu, Ni)+(Fe, Ni) zone or (Cu, Ni) zone.