Abstract:Domestic ceramics and 1Cr18Ni9Ti stainless steel were brazed using Ag-Cu-Ti filler metal. Microstructure,the component of characteristic points and the phases of brazing joints were studied by scanning electronic microscopy (SEM),energy distribution spectrometer (EDS) and x-ray diffraction (XRD). The results show that several kinds of intermetallics such as TiO2,TiO,TiSi2,Ti5Si3 and Fe2Ti were formed. The interfacial structure of joints is 1Cr18Ni9Ti stainless steel/Fe2Ti/Ag[s,s]+Cu[s,s]+Fe2Ti/TiO2+TiO+Ti5Si3+TiSi2/ceramics when brazing temperature and time are 850 ℃ and 5min,respectively. The depth of interfacial reactive layer increases and the ratio of matrix phase Ag[s,s],Cu[s,s] which are in the middle of interface reduces evidently as brazing temperature is very high or holding time is very long.

Interface structuce of ceramic/AgCuTi/stainless steel brazed joint