Abstract:A novel Ti-Ni-Si brazing filler metal was designed and fabricated to braze the C/C composite and C/C composite, and C/C composite and TiAl intermetallic alloy at 1060 °C for 10 min. The interfacial microstructures and mechanical properties were investigated, and the enhancing mechanism of the joint strength was elucidated. The results showed that a perfect interface joint was achieved by using TiNiSi to braze the C/C composite. Ductile Ti3SiC2 carbide was formed at the interface, which is beneficial to the joint bonding effect. The direct joining between the C/C composite and TiAl alloy using TiNiSi filler metal was unsuccessful, which was attributed to the high content of intermetallic compounds and hard–brittle phases in the brazed joint. The addition of a Cu interlayer to the joint can adjust the interfacial structure and reduce the content of brittle compounds, leading to a complete connection between the C/C composite and TiAl alloy. The interfacial transition layer on the C/C composite side mainly consisted of Ti3SiC2, Ti3AlC ductile ceramic phases, and TiC phase, which enhanced the performance of the brazed joint. The average shear strength at room temperature was 18.8 MPa, with the maximum value of 23.6 MPa, and the average shear strength at 600 °C was 25.8 MPa.

Interface Structure and Mechanical Properties of the Brazed Joint of TiC Cermet and Steel

Interface Structure and Bonding Strength of Brazed Joint of TiC Cermet/steel

Brazing temperature and time effects on the mechanical properties of TiC cermet/Ag–Cu–Zn/steel joints

Interface Structure and Strength of Brazed Joints Between TiC Ceramic and Iron

Interface structure and shear strength of brazed joints of TiAl-based alloy to middle-carbon steel

Microstructure and strength of TiC cermet/cast iron brazed with Ag – Cu – Zn filler metal

High Frequency Induction Brazing of TiC Cermets to Steel with Ag–Cu–Zn Foil

Interfacial Microstructure and Mechanical Property of ZrC-SiC Ceramic and Ti6Al4V Joint Brazed with AgCuTi Alloy

Interface microstructure and mechanical properties of the brazed SiO2 glass ceramic and 30Cr3 high-tensile steel joint

Effect of brazing time of TiC cermet/iron joint brazed with Ag-Cu-Zn filler metal

Ag–Cu–Zn Alloy for Brazing TiC Cermet/steel

Interface structure and mechanical properties of the TiAl/42CrMo steel joint vacuum brazed with Ag–Cu/Ti/Ag–Cu filler metal

Interfacial Microstructure and Properties of TiC Cermet and GH3128 Joint Brazed Using AgCuNiLi

Interface structure and mechanical property of the brazed joint of graphite and copper

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Research on the interfacial structure and mechanical properties of TC4-SiO2 composite brazed joint

Microstructure and Strength of the SiC/TiAl Joint Brazed with Ag-Cu-Ti Filler Metal

Improvement for Interfacial Microstructure and Mechanical Properties of Ti3SiC2/Cu Joint Brazed by Ag-Cu-Ti Filler with Copper Mesh

Microstructure Evolution and Mechanical Property of ZrC-SiC/Ti6Al4V Joints Brazed Using Ti-15Cu-15Ni Filler

Interfacial Microstructure and Properties of TZM Alloy and ZrCp-W Composite Joints Brazed Using Ti-50Ni Filler

Interface structure of brazing joint between hydrogenated TC4 titanium alloy and C/SiC composite