Interface structure and shear strength of brazed joints of TiAl-based alloy to middle-carbon steel

Jicai Feng,Huijie Liu

IF: 3.752

2003-01-01

Transactions of Nonferrous Metals Society of China

Abstract:Vacuum brazing of a TiAl-based alloy to a middle-carbon steel was carried out at 1 173 K for 0.5-40 min with a Ag-Cu filler metal. The formation phases and interface structure of the joints were investigated by SEM, EPMA and XRD, and the joint strength was determined by the shear test method. Three formation phases, Ti(Cu, Al)(2), Ag(s. s.) (Ag-based solid solution) and TiC, occurred in the brazing seam, and the interface structure of the joints can be expressed as TiAl/Ti(Cu, Al)(2) +Ag(s. s.)/Ag(s. s.)/TiC/steel, but TiC does not occur and a small amount of Ag-Cu eutectic exists in the joints brazed for a shorter time. The shear tests show that the room-temperature strength and fracture location of the brazed TiAl/steel joints change with brazing time. When the joint was brazed at 1 173 K for less than 2 min, the shear strength was up to 150 MPa and the fracture occurred within the Ti (Cu, Al)(2) +Ag(s. s.) zone.