Abstract:The residual stress is considered to be the driving force for the failure of ceramic/metal brazing joint. In this paper, the residual stress in a SiC/Nb joint is alleviated by using AgCuTi + B4C composite brazing filler. SEM, EDS and XRD are applied to characterised the microstructure of the joint, which is determined to be SiC/Ti3SiC2/Ag (s,s)+ Cu(s,s)+ TiB + TiC/TiCu + Nb(s,s)/Nb. The effects of the B4C strengthening phase mass fraction and the brazing temperature on the microstructure and the mechanical properties of the joint are investigated. It is found that the reaction products between B4C and the brazing filler (TiB whisker and TiC particles) uniformly distribute inside the joint if the mass fraction of the B4C is not higher than 1.5 wt% and when the amount of B4C reaches 2 wt%, the reaction products begin to agglomerate. With the rising of the brazing temperature, the thickness of the Ti3SiC2 reaction layer next to the ceramic increases and when the brazing temperature reaches 910 degrees C, another reaction layer of Ti5Si3 can be found adjacent to the Ti3SiC2 reaction layer. The strength of the joint first increases and then decreases with the increase of both the strengthening phase and the brazing temperature. The highest shear strength of the joint reaches 98 MPa when the joint is achieved at 890 degrees C using AgCuTi +1.5 wt%B4C brazing filler.

Interfacial Microstructure and Strength of Vacuum Brazed Joints of Ternary Ceramics Ti3SiC2

Understanding the Microstructure Evolution Mechanism and the Microstructure-Strength Correlations of Ti3SiC2/Ti2AlNb Joint Brazed with AgCu Interlayer

Microstructural Evolution of Si3n4/Ti6al4v Joints Brazed with Nano-Si3n4 Reinforced Agcuti Composite Filler

Microstructure and Mechanical Property of Vacuum Brazed SiC Ceramic Joint

Interfacial Microstructure and Mechanical Property of ZrC-SiC Ceramic and Ti6Al4V Joint Brazed with AgCuTi Alloy

Microstructural Evolution and Mechanical Properties of the Joint of TiAl Alloys and C/SiC Composites Vacuum Brazed with Ag–Cu Filler Metal

Microstructure and mechanical properties of Si3N4 ceramic and (TiB + Y2O3)/Ti matrix composite joints brazed with AgCu/Cu foam/AgCu multilayered filler

Microstructure and Mechanical Properties of the SiC/Nb Joint Brazed Using AgCuTi + B4C Composite Filler Metal

Interfacial microstructure and mechanical properties of porous-Si3N4 ceramic and TiAl alloy joints vacuum brazed with AgCu filler

Microstructure and Strength of the SiC/TiAl Joint Brazed with Ag-Cu-Ti Filler Metal

Interfacial Microstructure and Properties of In-situ TiB Reinforced ZrB2-SiC Joints

Interface microstructure and mechanism of SiC ceramic vacuum brazed joint

Microstructure and Formation Mechanism of Cf/SiC and Nb Joint Brazed with Laminated Amorphous Ti–Zr–Cu–Ni/crystalline Ti Composite Filler

Microstructure and Mechanical Property of Vacuum Brazed TiAl and C/SiC Joint

Interfacial Microstructure and Mechanical Properties of the Vacuum Brazed C/SiC Composite and Nb Joints

Interfacial Structure and Properties of Si3N4/AgCu/TiAl Brazing Joints

Interface Structure and Strength of Brazed Joints Between TiC Ceramic and Iron

Microstructure and Mechanical Properties of ZrB2–SiC Ultrahigh Temperature Ceramic Composite Joint Using TiZrNiCu Filler Metal

Interfacial Microstructure and Joining Properties of TiAl/Si3N4 Brazed Joints

Microstructure Evolution and Mechanical Property of ZrC-SiC/Ti6Al4V Joints Brazed Using Ti-15Cu-15Ni Filler

Interfacial microstructure and mechanical property of ZrC-SiC ceramic and TiAl joint brazed with AgZr active filler metal