Abstract:Brazing C/SiC composites and Nb is always trouble with high residual stress owing to high property, 'mismatch, especially in terms of the coefficient of thermal expansion. It weakens the joining strength and reduces the joining quality due to welding defects. The traditional method tends to modify the brazing alloy to overcome the problem of property mismatch by introducing reinforcement or interlayer. However, the application of these methods was limited by the low addition and poor distribution, thus inhibiting the development of brazing composites and alloy. as well as the use of composites. An increase in aircraft speed and size requires the composite-alloy joint to exhibit higher joining strength. To achieve this, heat penetration was employed to modify the composite surface of brazing C/SiC and Nb with the AgCuTi brazing alloy. It aims to provide a new idea for the design of the composite-alloy joint. In this study. the microstructure, residual stress distribution and reinforced mechanism of the joints were investigated in detail. Ni-Cr-Si alloy was introduced to penetrate due to the good reactive diffusion of Ni with SiC. The Ni2Si+C phase was in situ synthesized by replacing the SiC matrix and constructing the penetration zone using carbon fibers. The high strength and elasticity of the caibon fiber dispersed in the penetration zone increase the mechanical properties and decrease the brittleness. Moreover, the wettability of Ni-Cr-Si alloy on C/SiC composites improved as the Cr content increased. The ideal content of penetrating alloy was confirmed as Ni10Si15Cr (wt%). To reduce the brittleness of the composite-alloy joint. such content needs to be removed, so that bonding between alloys can be achieved. The typical microstructure of penetrated joints was C/SiC/C-1+Ni2Si+Cr3Ni2Si+Cr23C6/Ag(s,s)+(Cu.Ni)/Nb. The Cr elements were slightly diffused into the penetrating zone, thus reinforcing the bonding between carbon phases and Ni-Si compounds. The reaction layer of the compounds on C/SiC composites was replaced with the fiber reinforced penetration zone. The depth of this zone directly influenced the joining strength. To investigate in detail the penetration parameters, the penetration depth was optionally and homogeneously controlled. Accurate regulation of the penetration depth is beneficial for various application conditions. In addition, the reinforcing mechanism of penetration focused on the reduction of residual stress and enhancement of the C/SiC-alloy interface. In the penetration zone, the coefficient of thermal expansion gradually changed from C/SiC to AgCuTi alloy, which reduced the residual stress. The stress concentration of the C/SiC interface in the original joint was also eliminated. The fiber bundles supported the residual stress to prevent the appearance of cracks. Consequently, the residual stress in the brazing seam was reduced. The caibon fibers and dispersed phase enhanced the fracture strength and toughness of the penetrating zone. Fracture occurred in the penetration zone rather than in the reaction layer, with breaking and pulling out of fibers. A longer fracture path requires more energy for crack propagation. All these improvements contributed to the joining quality. The average shear strength increased from 85.5 to 115.2 MPa, with a penetrating depth of 77 mu m. The penetration treatment of C/SiC composites provides a new method of brazing composites to alloy. Such method is suitable for different brazing alloys and various brazing requirements. Moreover, it enables the surface modification of composites. Thus, it is important to pay attention to the crucial effect of fiber reinforcement on composites. This research aimed to efficiently expand the application of composites and dissimilar joints.

Interfacial Microstructure and Mechanical Properties of the Vacuum Brazed C/SiC Composite and Nb Joints

Effects of surface state of C/SiC composites on brazing of C/SiC to Nb

Brazing C/SiC Composites and Nb with TiNiNb Active Filler Metal

Microstructure and Formation Mechanism of Cf/SiC and Nb Joint Brazed with Laminated Amorphous Ti–Zr–Cu–Ni/crystalline Ti Composite Filler

Interfacial microstructure and mechanical properties of TiAl and C/SiC joint brazed with TiH2-Ni-B brazing powder

Microstructure Evolution and Mechanical Properties of SiC and Nb Joint Brazed with AgCuTi/(Sr0.2Ba0.8)TiO3-Cu/AgCuTi Composite Fillers

Microstructure and Mechanical Property of Vacuum Brazed TiAl and C/SiC Joint

Microstructure and Mechanical Properties of the SiC/Nb Joint Brazed Using AgCuTi + B4C Composite Filler Metal

Interfacial Microstructure and Mechanical Properties of C/C Composites and Nb Joints Brazed with Cu75Pt25 Filler Metal

Joints of Continuous Carbon Fiber Reinforced Lithium Aluminosilicate Glass Ceramics Matrix Composites to Ti60 Alloy Brazed Using Ti-Zr-Ni-Cu Active Alloy

Interface microstructure and mechanism of SiC ceramic vacuum brazed joint

Vacuum Brazing Nb and Bn-Sio2 Ceramic Using A Composite Interlayer with Network Reinforcement Architecture

Microstructure and Mechanical Properties of Cf/SiC Composite/gh99 Joints Brazed with BNi2-Ti Composite Filler

Microstructure and properties of different carbon fiber reinforced ceramic composites brazed joint by Si-Ti alloy filler

Microstructure and mechanical properties of ZrB2-SiC ceramic composite brazed joint

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Vacuum Brazing of C/C Composite and TiAl Intermetallic Alloy Using BNi-2 Brazing Filler Metal

Microstructure and Mechanical Property of Vacuum Brazed SiC Ceramic Joint

Microstructure Improvement of C/SiC-Nb Brazing Joint S Reinforced with Heat Penetration

Microstructural Evolution and Mechanical Properties of the Joint of TiAl Alloys and C/SiC Composites Vacuum Brazed with Ag–Cu Filler Metal

Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler