Experimental investigation on the fatigue life and damage mechanism of plain weave composites under biaxial tension–torsion combined fatigue loading
Zhanguang Chen,Tao Zheng,Rongqing Sun,Li Zhang,Zhongyu Wang,Jindi Zhou,Xiaojian Han,Shangyang Yu,Licheng Guo
DOI: https://doi.org/10.1016/j.ijfatigue.2024.108425
IF: 5.489
2024-06-12
International Journal of Fatigue
Abstract:In this paper, the fatigue life and damage mechanism of plain weave composites under biaxial tension–torsion combined fatigue loading (TTF) are experimentally investigated. A biaxial TTF loading spectrum is designed to consider different fatigue frequencies and amplitudes, and an automated multi-module loading method with synchronized acquisition of the digital image correlation (DIC) and the testing machine is proposed. A comprehensive analysis of the experimental results, including fatigue lives, strain distribution, temperature variation, stiffness degradation, and typical damage morphologies at different fatigue cycles, has been conducted by utilizing DIC, infrared thermography (IRT) and computed tomography (CT). It is observed that the superimposed torsional fatigue load results in a rapid reduction in fatigue lives of plain weave composites, accompanied by more significant residual strain, energy dissipation, temperature rise and stiffness degradation. Particularly, the superimposed torsional fatigue loads mainly promote matrix cracking and debonding around the fiber/matrix interfaces, which then accelerates the damage initiations and accumulations of fiber yarns, ultimately leading to a rapid reduction in TTF fatigue lives. This study can provide valuable references for the design and safe application of plain weave composites under TTF loading.
materials science, multidisciplinary,engineering, mechanical