Band-Gap Engineering of FeF 3 ·0.33H 2 O Nanosphere via Ni Doping as a High-Performance Lithium-Ion Battery Cathode
Min Liu,Qun Wang,Biaobing Chen,Huiling Lei,Lei Liu,Chun Wu,Xianyou Wang,Zhenhua Yang
DOI: https://doi.org/10.1021/acssuschemeng.0c05258
2020-09-17
Abstract:Iron-based fluorides, a kind of intercalation–conversion cathode material, are considered as one of the most promising candidate cathode materials for lithium-ion batteries due to their high capacity and cheap cost. Nevertheless, poor electrical conductivity and sluggish reaction kinetics upon cycling impede their practical application. Herein, Ni-doped FeF<sub>3</sub>·0.33H<sub>2</sub>O has been put forward and fabricated by a simple solvothermal method to overcome the above deficiency. The impact of Ni doping on the physical and electrochemical performances has been studied by first-principles calculations combined with comprehensive physicochemical characterizations. The results reveal that appropriate substitution of Fe sites by Ni can result in F vacancies without changing the intrinsic crystal structure, but it not only reduces the band gap and improves its intrinsic conductivity but also broadens the ion channel, thus facilitating the rapid transport of ions and electrons to acquire excellent electrochemical properties. Compared with the bare FeF<sub>3</sub>·0.33H<sub>2</sub>O, the appropriate amount (8%) of Ni<sup>2+</sup> doping exhibits higher reversible capacity, longer cyclic stability, and better rate capability. It presents a 412 mAh g<sup>–1</sup> initial discharge capacity and remains 264 mAh g<sup>–1</sup> after 100 cycles at 0.25 C (1 C = 200 mA g<sup>–1</sup>) within a range of 1.5–4.5 V. Additionally, at 2.0 C, it still delivers a high discharge capacity of 248 mAh g<sup>–1</sup>. The excellent electrochemical performance is ascribed to the improvement of electronic conductivity and reaction kinetics caused by the moderate Ni doping.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c05258?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c05258</a>.Long-term stability, SEM figure, and mole ratios (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c05258/suppl_file/sc0c05258_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology