Co-precipitation synthesis and performance of multi-doped LiCr x Ni x Mn 2-2x O 4-z F z cathode materials for lithium ion batteries

Ronghua Li,Feiyan Gong,Wenji Wang

DOI: https://doi.org/10.1007/s11581-006-0056-9

IF: 2.961

2007-01-01

Ionics

Abstract:Multiple ion-doped lithium manganese oxides LiCr x Ni x Mn 2-2x O 4-z F z (0 < x ≤ 0.25, z = 0.05, 0.1) with a spinel structure and space group Fd 3 m were prepared by using the co-precipitation procedure carried out in water–alcohol solvent using adipic acid as the chelating agent. The electrochemical measurements indicated that the charge/discharge capacities of the samples prepared at 600 °C are higher than that of the treatment at 800 °C or microwave heating. The capacitance-voltage (CV) curves of LiCr x Ni x Mn 2-2x O 4-z F z (0 < x ≤ 0.25, z = 0.05, 0.1) showed that when x ≤ 0.1, the samples had two reduction–oxidation peaks at 4.0 to 4.2-V region, whereas when x > 0.1, the samples had only one reduction–oxidation peak at 4.0- to 4.2-V region in CV measurements and could offer more stable voltage plateau in a 4-V region and also had stable electrical conductivity after 20 cycles. Another reduction–oxidation peak appeared in 4.6-4.8-V region (Ni 2+ –Ni 4+ reduction–oxidation peaks); this suggests that the LiCr x Ni x Mn 2-2x O 4-z F z (0.1 < x ≤ 0.25, z = 0.05, 0.1) cathode material could offer 4.6 to 4.8-V charge/discharge plateaus, and its specific capacity increases with increasing Ni 2+ . The impedance measurements of the cell proved that the F − anion doped can not only prevent Mn 3+ from disproportion but also can prevent the passivation film from forming and can help keep stable the cell’s electrical properties. The LiCr 0.05 Ni 0.05 Mn 1.9 O 3.9 F 0.1 sintered at 600 °C shows the best cycle performance and the largest capacity in all prepared samples; its first discharge capacity is 120 mAh/g, and the discharge capacity loses only 1.78