High temperature solid-state synthesis and characterization of 5V anode LiNi0.5Mn1.5O4-xFx materials

Jing Luo,Jiangang Li,Jianjun Li,Xiangming He

DOI: https://doi.org/10.3969/j.issn.1006-3536.2013.01.032

2013-01-01

Abstract:5V anode LiNi0.5Mn1.5O4-xFx(x=0,0.025,0.05,0.075 and 0.1)materials were prepared via high temperature solid-state reaction.Effects of annealing temperature and F-doping amount on structure and properties of the products were investigated by using XRD,SEM,electrochemical impedance spectra(EIS)and charge-discharge tests.XRD and SEM results indicated that the phase purity,crystallinity and particle size of LiNi0.5Mn1.5O4-xFx depend on both annealing temperature and F-doping amount.The F-doping amount 0.05~0.075 products annealed at 850℃ had pure spinel phase with high crystallinity,moderate and uniform particle size.The electrochemical tests showed that all samples exhibited good cycling stability,and F-doping improved the capacity and rate capability of LiNi0.5Mn1.5O4.The product with F-doping amount 0.05 had the smallest film resistance and charge transfer resistance,and showed higher capacity and the best rate capability.Its 0.2C discharge capacity reached 128.5mAh·g-1,and retained 93.8% at 2C after 40 cycles.The 2C/0.2C capacity ratio of undoped sample only retained 71.8% in the same test condition.