Abstract:Developing ultra-high strength in rare-earth-free Mg alloys using conventional extrusion process is a great challenge. What is even more difficult is to achieve such a goal at a lower processing cost. In this work, we report a novel low-alloyed Mg-2Sn-2Ca alloy (in wt. %) that exhibits tunable ultra-high tensile yield strength (360–440 MPa) depending on extrusion parameters. More importantly, there is little drop in mechanical properties of this alloy even when it is extruded at a speed several times higher than those used in the reported high strength Mg alloys. Examination of as-extruded microstructures of this Ca-containing Mg alloy reveals that the ultra-high strength is mainly associated with the presence of surprisingly submicron matrix grains (down to ∼0.32 μm). The results suggest that the Ca addition promotes accumulations of the pyramidal dislocations, which eventually transform into the low angular grain boundaries (LAGBs). The high number density of LAGBs separate the α-Mg matrix via either discontinuous dynamic recrystallization (DDRX) mechanism in the early stage or the continuous dynamic recrystallization (CDRX) mechanism in the later stage of extrusion, which effectively enhances the nucleation rates of the DRXed grains. More importantly, large amount of Ca segregation along LAGBs, accompanied with dynamically precipitated Mg2Ca nano-phases, are detected in the present non-severely deformed samples. It is the combination of solute segregations and numerous Mg2Ca nano-precipitates that contributes to the formation of the ultra-fine grains via pinning mechanism. The ultrafine grains size, Ca enrichment in most LAGBs, and residual Mg2Ca nano-precipitates would in turn contribute significantly to the enhancement of the yield strength of the as-extruded Mg-2Sn-2Ca (wt.%) alloy. The low content of alloying elements and the fast one-step extrusion process render the present alloys low-cost and thus have great potential in large-scale industry applications.

Development of Mg–6Al–4Sn–1Zn Alloy Sheets with Ultra-High Strength by Combining Extrusion and High-Speed Rolling

Development of low-alloyed and rare-earth-free magnesium alloys having ultra-high strength

A high-performance Mg-Al-Sn-Zn-Bi alloy fabricated by combining sub-rapid solidification and hot rolling

Development of low-alloyed Mg–Zn–Ca–Sn–Mn alloy with high strength-ductility synergy by sub-rapid solidification and hot rolling

Enhancing Mechanical Properties of Rolled Mg-Al-Ca-Mn Alloy Sheet by Zn Addition

Novel Mg–Al–Sn–Zn–Y Alloys with Enhanced Strength−Ductility Combination Prepared by Hard‐Plate Rolling

Improving Strength and Ductility of Mg–Gd–Y–Zn–Zr Alloy Simultaneously Via Extrusion, Hot Rolling and Ageing

Realizing ultra-fine grains and ultra-high strength in conventionally extruded Mg-Ca-Al-Zn-Mn alloys: The multiple roles of nano-precipitations

An Mg‐Al‐Zn Alloy with Verry High Specific Strength and Superior High‐strain‐rate Superplasticity Processed by Reciprocating Extrusion

Dynamic precipitation and twinning-induced dynamic recrystallization in Mg–6Al–3Sn–1Zn alloy during multi-pass high-speed rolling

Ultra High-Strength Mg–Gd–Y–Zn–Zr Alloy Sheets Processed by Large-Strain Hot Rolling and Ageing

On Mechanical Properties and Superplasticity of Mg–15Al–1Zn Alloys Processed by Reciprocating Extrusion

Fabrication of high strength-ductility Mg-3.8Al-1.1Sn-0.4Ca alloy via differential-thermal asymmetric extrusion

Evolution of Bimodal-Structure and Achieving Ultra-High Yield Strength in the As-Extruded ZK70 Alloy Via Gd Addition

A high-strength low-rare-earth-alloyed magnesium alloy via traditional hot-extrusion

Ultra strength-ductility synergy in the Mg-Al-Zn alloy via densely dispersed multi-scale {1012‾} tension twins

Developing Mg-Gd-Dy-Ag-Zn-Zr Alloy with High Strength via Nano-Precipitation

High strength-ductility synergy and low anisotropy of Mg-4.5Al-2.6Zn-0.3Mn alloy sheet achieved by annealing after rolling

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

Achieving Low Tension-Compression Yield Asymmetry and Ultrahigh Strength in Mg–1Al–1Ca–0.2Mn (wt%) Alloy Via Sub-Micron Grain Refinement