Abstract:In this study, 5083 aluminum alloys modified with grain refiner, 0.25% Zr and 0.46% Mn, were processed by reciprocating extrusion to yield high-strain-rate superplasticity above 400°C and superior room-temperature mechanical properties. Without any prior homogenization treatment, 10 extrusion passes could give the cast billets an equiaxed grain structure with a grain size of about 4.5μm and a subgrain size about 0.2μm, and a uniform distribution of fine inclusions and dispersoids in the matrix. The fine-grained structure was stable up to 525°C, giving the alloy a high-strain-rate and low-stress superplasticity over a wide operating temperature of 400–500°C. In the tensile test at 500°C, a maximum elongation of 1013% and a low flow stress of 7.7MPa at 5×10−2s−1 were achieved. The apparent and true activation energies for low temperatures (300–400°C) without high-strain-rate superplasticity were 220.6 and 208kJ/mol, respectively, whereas those at high temperatures (400–500°C) were 88.4 and 98.7kJ/mol, respectively. Further analysis confirms that grain boundary sliding is the dominant mechanism over the high-strain-rate region from 1×10−2 to 5×10−1s−1 at 500°C, and power-law breakdown mechanism occurs over the strain rate from 5×10−4 to 1×10−2s−1 at 300°C. The high-strain-rate superplasticity was more strongly enhanced by Zr addition than addition of Cr and Mn. Two enhancing mechanisms for the maximum superplastic elongation and the optimum strain rate are proposed. This study concludes that the effectiveness of Zr is caused by the fineness and the coherency of Zr-rich dispersoids in the matrix.

An Mg‐Al‐Zn Alloy with Verry High Specific Strength and Superior High‐strain‐rate Superplasticity Processed by Reciprocating Extrusion

On Mechanical Properties and Superplasticity of Mg–15Al–1Zn Alloys Processed by Reciprocating Extrusion

Microstructural evolution and superplasticity of Al-5.8Mg-0.23Mn alloys processed by reciprocating extrusion

A High-Strength Extruded Mg-Gd-Zn-Zr Alloy with Superplasticity

High Strain Rate Superplasticity in Al-Zn-Mg-Based Alloy: Microstructural Design, Deformation Behavior, and Modeling

Superplasticity of 5083 Alloys with Zr and Mn Additions Produced by Reciprocating Extrusion

Superplastic Behavior of an Extruded Mg-Zn-Y-Zr Alloy

High Performance Mg Alloy with Designed Microstructure and Phases

High Strain Rate Quasi-Superplasticity Behavior in an Ultralight Mg-9.55Li-2.92Al-0.027Y-0.026Mn Alloy Fabricated by Multidirectional Forging and Asymmetrical Rolling

A high-performance Mg-Al-Sn-Zn-Bi alloy fabricated by combining sub-rapid solidification and hot rolling

Superplasticity of Mg-5.8Zn-1Y-Zr Alloy Sheet Fabricated by Combination of Extrusion and Hot-Rolling Processes

Realizing impressive superplasticity in a low-alloyed Mg-Zn-Ca-Al-Mn alloy: The roles of grain boundary segregation and dense β-Mn particles

Achieving Ultra-High Strength and Ductility in Mg–9Al–1Zn–0.5Mn Alloy Via Selective Laser Melting

A novel die-casting Mg alloy with superior performance: Study of microstructure and mechanical behavior

Heterogeneous Fiberous Structured Mg-Zn-Zr Alloy with Superior Strength-Ductility Synergy

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

Origins of High Ductility Exhibited by an Extruded Magnesium Alloy Mg-1.8Zn-0.2Ca: Experiments and Crystal Plasticity Modeling

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Investigation of Microstructures and Mechanical Properties of Ultra-High Strength Al-Zn-Mg-Cu Alloy Prepared by Rapid Solidification and Hot Extrusion

Superplastic Behaviors of a Mg–Zn–Y–Zr Alloy Processed by Extrusion and Equal Channel Angular Extrusion

Achieving high strain rate superplasticity in an Al-Cu-Li alloy processed by thermo-mechanical processing