Abstract:The role of Ca content (0.5, 1.0, 2.0 wt.%) on microstructure, mechanical properties and strain evolution of as-rolled Mg-Al-Ca-Zn-Mn alloy was thoroughly investigated in this work. The results indicate that the primary second phase transformed from the Mg17Al12 phase to the Al2Ca phase after homogenization, and the amount of Al2Ca phase increased significantly with increasing Ca content. After hot rolling, the alloys exhibited the typical bimodal microstructure composed of fine dynamic recrystallized (DRXed) grains and coarse elongated un-DRXed grains, the area fraction of the DRXed regions increased with increasing Ca content. Besides, a large number of submicron-sized as well as nano-scaled spherical Mg17Al12 phases dynamically precipitated along the DRXed grain boundaries in all alloys, which promoted the DRX and restricted the grain growth. During rolling deformation, DRX preferentially occurred near the primary second phases and shear bands by the particle stimulated nucleation (PSN) and shear band induced nucleation (SBIN) mechanism in the alloys. The ultimate tensile strength (UTS), yield strength (YS), and elongation to failure (EF) along the rolling direction (RD) of the Mg-8.0Al-1.0Ca-1.0Zn-0.4Mn (wt.%) sheet were 393 MPa, 334 MPa and 8.7 %, respectively. Such high strength was mainly attributed to fine DRXed grains, high number density of dynamically precipitated Mg17Al12 phases and strongly textured un-DRXed grains with numerous sub-structures. The reasonable DRX ratio moderated strain localization and thus stabilized tensile deformation, leading to moderate plasticity of the alloy.

Enhancing Mechanical Properties of Rolled Mg-Al-Ca-Mn Alloy Sheet by Zn Addition

Development of Corrosion-Resistant Mg-Al-Ca-Mn-Zn Alloy Sheet with Good Tensile Properties and Stretch Formability

Achieving High Strength in Micro-alloyed Mg-Al-Ca-Zn-Mn-Ce Alloy Sheet Processed by Single-Pass Large-Strain Rolling

High strength-ductility synergy and low anisotropy of Mg-4.5Al-2.6Zn-0.3Mn alloy sheet achieved by annealing after rolling

Effect of Reduction in Thickness and Rolling Conditions on Mechanical Properties and Microstructure of Rolled Mg-8Al-1Zn-1Ca Alloy

Improving Formability of Mg–Ca–Zr Sheet Alloy by Microalloying of Zn

Role of Ca Content on Microstructure, Mechanical Properties and Strain Evolution of As-Rolled Mg-Al-Ca-Zn-Mn Alloy

Achieving High Ductility in Hot-Rolled Mg-xZn-0.2Ca-0.2Ce Sheet by Zn Addition

A Rolled Mg‐8Al‐1Sm‐1Zn Alloy with High Strength‐Ductility via Single‐Pass Liner Rolling

Development of Mg–6Al–4Sn–1Zn Alloy Sheets with Ultra-High Strength by Combining Extrusion and High-Speed Rolling

Dramatic Improvement of Formability in Mg-3Al-1Sn-0.5Ca-0.1Sm Alloy Via Mn Microalloying Combined with High Temperature Rolling

Microstructure and Mechanical Properties of Mg-Gd-Y-Zn-Mn Alloy Sheets Processed by Large-Strain High-Efficiency Rolling

Property Improvements in Fine–grained Mg–Zn–Zr Alloy Sheets Produced by Temperature–step–down Multi–pass Rolling

Development of Weak-Textured and High-Performance Mg–Zn–Ca Alloy Sheets Based on Zn Content Optimization

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

Strength-ductility balance of Mg-1.03Ca-0.47Mn Mg alloy sheet produced by rolling and annealing

Developing High-Strength and Ductile Mg-Gd-Y-Zn-Zr Alloy Sheet Via Bimodal Grain Structure Coupling with Heterogeneously-Distributed Precipitates

Development of High Strength and Formability Mg-6Zn-0.2Ca Alloy Via Multi-Pass Warm Rolling and Aging Treatment

Microstructure, Texture and Mechanical Properties of Mg-Sn-Zn Alloy Sheets Processed by Extrusion and Hot Rolling

Development of low-alloyed Mg–Zn–Ca–Sn–Mn alloy with high strength-ductility synergy by sub-rapid solidification and hot rolling

Microstructure and Mechanical Property of High Strength Mg–Sn–Zn–Al Alloys