High fatigue performance and microscopic mechanisms of in-situ TiB 2 /7050Al composite at different temperatures
Liufang Ma,Xian Luo,Hong Wang,Rui Hu,Xiaowei Yi,Chaoxian Zhou,Wei Chen,Gang Ran
DOI: https://doi.org/10.1016/j.ijfatigue.2024.108372
IF: 5.489
2024-05-06
International Journal of Fatigue
Abstract:In this work, the fatigue properties of in-situ TiB 2 particle-reinforced 7050 Al-matrix (TiB 2 /7050Al) composites at room temperature (RM), 100 °C and 150 °C were studied, respectively, and the microstructure changes, fatigue fracture characteristics and fracture mechanism were analyzed. The results indicate that when the fatigue temperature increased, the amount of S phase precipitation along grain boundaries increases, forming a banded distribution with TiB 2 particles near the grain boundary regions. The RM fatigue limit of the composite is high up to 307.5 MPa. Under the same fatigue strength, TiB 2 /7050 composites can withstand fatigue cycles far greater than 7050Al alloy. With the increase of temperature, the fatigue performance of the composite gradually decreased, and unlike at RM and 100 °C, the use of Weibull three-parameter model is necessary to obtain a satisfactory S - N curve at 150 °C. In some locations of the steady-state crack propagation stage, the direction and spacing of fatigue striations were influenced by grain orientation, grain boundaries and TiB 2 particle bands. Therefore, the effects of TiB 2 particles, grain boundaries, and precipitations on the fatigue processes were analyzed to reveal the strengthening mechanisms of the composite.
materials science, multidisciplinary,engineering, mechanical