Abstract:To gain insights into the relationship between the fracture behavior and the unique microstructure of the in situ TiB2/2024 Al composite, systematic experiments were conducted over wide ranges of temperature (298–673 K), strain rate (0.001–4000/s), and stress triaxiality (−0.82–1.03). The results showed that the strengthening mechanism of the composite was related to Orowan strengthening and coefficient of thermal expansion (CTE) mismatch strengthening. Owing to the smaller particle size and sturdy interfacial bonding, the tensile strength of the in situ nano/submicron TiB2/2024 composite was higher than that of the ex situ composite and the in situ micron composite. Through a morphologic study by scanning electron microscopy (SEM), the microstructural deformation and crack propagation path were found to be largely dependent on the stress state, strain rate, and temperature. The melted matrix precipitated in the dynamic tensile fracture surface can hinder the crack propagation and is considered the determining factor that improves the ductility at room temperature. Furthermore, a 3D fracture locus in the space of the fracture strain, stress triaxiality, and the Lode angle parameter was formed. Finally, a new fracture criterion that considers the Lode angle parameter, the stress triaxiality cutoff value, and the coupling effect of strain rate and temperature was developed. The developed criterion exhibited a robust and accurate capability to describe the fracture behavior of the in situ TiB2/2024 Al composite.

Experimental study of the mechanisms of nanoparticle influencing the fatigue crack growth in an in-situ TiB2/Al-Zn-Mg-Cu composite

Microstructural correlated damage mechanisms of the high-cycle fatigued in-situ TiB2/Al-Cu-Mg composite

High Cycle Fatigue Behavior of the In-Situ TiB2/7050 Composite

Effects of stress state, strain rate, and temperature on fracture behavior of in situ TiB2/2024 Al composite

Study fatigue crack initiation in TiB2/Al-Cu-Mg composite by in-situ SEM and X-ray microtomography

Deformation-induced ultrafine grains near fatigue crack tip and correlative fatigue damage in Al matrix composite

Study fatigue crack initiation in TiB<sub>2</sub>/Al-Cu-Mg composite by <i>in-situ</i> SEM and X-ray microtomography

Study on Microscopic Ductile Fracture of In-Situ TiB2/2024 Al Matrix Composite

High fatigue performance and microscopic mechanisms of in-situ TiB 2 /7050Al composite at different temperatures

High Fatigue Performance and Microscopic Mechanisms of In-Situ TiB2/7050Al Composite at Different Temperatures

Study on fracture mechanism and fatigue life prediction for cutting insitu tib2/7050al mmcs

Fatigue Behavior of In-Situ TiB2/7050Al Metal Matrix Composites: Fracture Mechanisms and Fatigue Life Modeling after Milling

Revealing the complex effects of particle bands on fatigue crack growth in an extruded aluminium matrix composite

Numerical Simulation of Fracture Behavior of In-Situ TiB2 Particle Reinforced 2024-T4 Aluminum Matrix Composites

Effects of three stress levels on the fatigue properties and fracture mechanisms of an in-situ synthesized TiB/Ti-6Al-4V titanium matrix composite

Stress Corrosion Cracking Behavior of In-Situ TiB2/7050 Composite

Microstructural Influences on the High Cycle Fatigue Life Dispersion and Damage Mechanism in a Metastable Β Titanium Alloy

Fatigue Crack Initiation and Propagation in A356 Alloy Reinforced with in Situ TiB2 Particles

Fatigue Crack Initiation and Propagation Dominated by Crystallographic Factors in TiB/near α-Ti Composite

Revealing the Effect of Oriented Microstructures on the Anisotropy of Fatigue Crack Propagation Behavior in TiB2/Al-Cu-Mg-Mn Composite

Ductile Fracture Behavior of in Situ TiB2 Particle Reinforced 7075 Aluminum Matrix Composite in Various Stress States