Abstract:In mechanical applications, defect-based fatigue cracking is a significant strength-limiting failure mode of additively manufactured composites that is not yet fully understood in the service environment. In this paper, axial loading tests were carried out at 25 °C and 450 °C, and then the effects of temperature on the long-life fatigue properties of the TiC-reinforced Ti6Al4V composite fabricated by Laser Powder Bed Fusion (LPBF) were investigated by combining the techniques of electron backscatter diffraction, X-ray computed tomography, and 3D morphological reconstruction. With the increase in temperature, the fatigue strength of the LPBF TiC/Ti6Al4V composite decreases significantly. The main causes of the interior failure at both temperatures are the inhomogeneous hardening zone (IHZ) formed by TiC agglomeration and the pore defect generated during the manufacturing process. The presence of brittle IHZ and pores causes stress concentration, which leads to crack nucleation. When a crack reaches the specimen surface, the combined effects of temperature and oxygen accelerate the ensuing crack propagation at high temperature. Based on the temperature effect, material properties, and the statistical distribution of defects, a model has been developed to predict the P-S-N curves at both temperatures. This model performed well in estimating the fatigue strength at 10 9 cycles. These findings provide new insights into the defect-related fatigue failure mechanisms and strength evaluation of the LPBF TiC/Ti6Al4V composite at different temperatures.

High Fatigue Performance and Microscopic Mechanisms of In-Situ TiB2/7050Al Composite at Different Temperatures

High fatigue performance and microscopic mechanisms of in-situ TiB 2 /7050Al composite at different temperatures

High Temperature Tensile Properties of in Situ TiBw/Ti6Al4V Composites with a Novel Network Reinforcement Architecture

High Cycle Fatigue Behavior of the In-Situ TiB2/7050 Composite

Effects of stress state, strain rate, and temperature on fracture behavior of in situ TiB2/2024 Al composite

Fatigue Behavior of In-Situ TiB2/7050Al Metal Matrix Composites: Fracture Mechanisms and Fatigue Life Modeling after Milling

Investigation on Surface Roughness, Residual Stress and Fatigue Property of Milling In-Situ TiB 2 /7050al Metal Matrix Composites

Investigation on the High-Temperature Ductility and Fracture Mechanisms of an In-Situ Particle Reinforced Al Matrix Composite 7075Al/tib2

Effects of three stress levels on the fatigue properties and fracture mechanisms of an in-situ synthesized TiB/Ti-6Al-4V titanium matrix composite

Microstructural correlated damage mechanisms of the high-cycle fatigued in-situ TiB2/Al-Cu-Mg composite

Defect-based fatigue crack nucleation and strength evaluation of additively manufactured TiC/Ti6Al4V titanium matrix composite at different temperatures

Fatigue Crack Initiation and Propagation in A356 Alloy Reinforced with in Situ TiB2 Particles

Impact behavior of in situ TiB<sub>2</sub>/Al composite at various temperatures

Impact behavior of in situ TiB 2 /Al composite at various temperatures

Experimental study of the mechanisms of nanoparticle influencing the fatigue crack growth in an in-situ TiB2/Al-Zn-Mg-Cu composite

Microstructural Influences on the High Cycle Fatigue Life Dispersion and Damage Mechanism in a Metastable Β Titanium Alloy

Compressive response and microstructural evolution of in-situ TiB2 particle-reinforced 7075 aluminum matrix composite

Damage mechanism of TiB;/2024Al composite in high-cyclic fatigue

The Relationship Between TiB2 Volume Fraction and Fatigue Crack Growth Behavior in the in Situ TiB2/A356 Composites

Mechanical responses of in-situ TiB2/7050 composite subjected to monotonic and cyclic loadings: A comparative study with 7050-Al

High Cycle Fatigue Behaviors and Deformation Mechanisms in Ti47Al2Cr2Nb Alloy at Room Temperature and 700 °C