Abstract:This work designed a novel TiNiCuNb eutectic alloy for manufacturing C/C-SiC composite joints. By introducing Ti into the semi-solid TiNiCuNb alloy, low-temperature melting of this eutectic alloy was induced. Ti/TiNiCuNb/ Ti composite interlayers were utilized to join C/C-SiC composite lower than the melting temperature of TiNiCuNb alloy. Effects of joining temperature on the microstructure evolution and mechanical property of joints were investigated. The melting range of this TiNiCuNb alloy was 944 degrees C to 1064 degrees C. During the initial melting of the TiNiCuNb alloy, a thin liquid layer formed on the alloy's surface, which provided a path for the rapid diffusion of elements. Without pressure, Ti could be easily introduced into the TiNiCuNb alloy, which induced the complete melting of this alloy at 950 degrees C. Based on this, we successfully brazed C/C-SiC composite using Ti/ TiNiCuNb/Ti interlayers. It not only hindered the formation of brittle compounds in the joints, but also weakened the overreaction between filler and C/C-SiC composite. Due to the high solubility of Si in liquid filler, the joint microstructure was controlled by the interaction between filler and SiC at different temperatures. At 1010 degrees C for 10 min, the maximum shear strength of 28.5 MPa was obtained. This work contributed to preparing and repairing the C/C-SiC composite.

Inducing Low-Temperature Melting of TiNiCuNb Eutectic Alloy for Manufacturing Strong C/C-SiC Composite Joints

Joining C/C–SiC Composite and Ti60 Alloy Using a Semi-Solid TiNiCuNb Filler

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Interfacial microstructure and mechanical properties of TiAl and C/SiC joint brazed with TiH2-Ni-B brazing powder

In-situ stabilized β-Ti in Ti-base alloys to enhance Cf/SiC-Nb heterogenous joint

In Situ TiSi2 Microarray Reinforced Si–Ti Eutectic Colonies in Cf/C Composite Joints for High-Temperature Application

Microstructure Evolution and Brazing Mechanism of Ti5Si3/Ti3Al Composite and Ni-based Superalloy Joints Using Ti-Zr-Cu-Ni Filler Alloy

Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler

Brazing of C/C Composite to TiAl Alloy Using (ti/ni/cu)f Multi-foil Filler

Interfacial Microstructure and Mechanical Properties of the Vacuum Brazed C/SiC Composite and Nb Joints

SiC fiber strengthened Si-14Ti high-temperature filler alloy for brazing SiCf/SiC and C/C composites

Microstructure and Formation Mechanism of Cf/SiC and Nb Joint Brazed with Laminated Amorphous Ti–Zr–Cu–Ni/crystalline Ti Composite Filler

Wetting of Si–14Ti Alloy on SiCf/SiC and C/C Composites and Their Brazed Joint at High Temperatures

Microstructure and mechanical properties of C/C composite joint brazed with Ni-based filler

Brazing of Ti-coated SiC Using a CoFeCrNiCu High Entropy Alloy Filler Via Electric Field-Assisted Sintering

SiC fiber strengthened Si 14Ti high-temperature filler alloy for brazing SiC f /SiC and C/C composites

Brazing C/SiC Composites and Nb with TiNiNb Active Filler Metal

Microstructure and mechanical properties of C f /SiC composite joints joined using AlCoCrFeNi 2.1 eutectic high-entropy alloy filler via spark plasma sintering

Microstructure Evolution and Mechanical Property of ZrC-SiC/Ti6Al4V Joints Brazed Using Ti-15Cu-15Ni Filler

A Study of the SiCf/SiC Composite/ni-Based Superalloy Dissimilar Joint Brazed with a Composite Filler

A Novel Composite Interlayer Assembled for C/SiC-GH99 Brazed Joints