Abstract:The brazing of C/C and C f /SiC composites was achieved using Si–14Ti eutectic filler. The wetting behavior of the Si–Ti filler on the composites, as well as the microstructure and performance of the joints at different brazing temperatures, were characterized. The results showed that the contact angle of Si–Ti eutectic filler on precursor infiltration and pyrolysis (PIP)-C f /SiC composite surface is only 60°, while it exhibits good spreading effect on liquid silicon infiltration (LSI)-C f /SiC and C/C composite surfaces. Although Si–Ti filler and carbon fiber reinforced composites (C/C, PIP-C f /SiC and LSI-C f /SiC) react to form SiC, the joint shows different mechanical performance. The liquid filler infiltrates into the gaps between fiber bundles and reacts with C/C to form a SiC reaction layer at the interface. However, the presence of numerous defects at the brazed joint between Si–Ti filler and PIP-C f /SiC results in the shear strength of only 28 MPa for the C/C-PIP-C f /SiC joint. While for the C/C-LSI-C f /SiC joint, due to the residual Si in the LSI-C f /SiC composites, the liquid filler infiltrates intensely into LSI-C f /SiC to form a unique C f /SiC–Si–TiSi 2 compound infiltration layer. The shear strength of C/C-LSI-C f /SiC joints reaches 47 MPa, with fracture occurring in both substrates and brazed seam. The present study offers theoretical support for the investigation of Si-based fillers in brazing carbon fiber reinforced ceramic matrix composites.

Wetting of Si–14Ti Alloy on SiCf/SiC and C/C Composites and Their Brazed Joint at High Temperatures

SiC fiber strengthened Si-14Ti high-temperature filler alloy for brazing SiCf/SiC and C/C composites

SiC fiber strengthened Si 14Ti high-temperature filler alloy for brazing SiC f /SiC and C/C composites

Wetting and brazing of Cf/C composites with Si–Zr eutectic alloys: The formation of nano- and coarse-SiC reaction layers

Microstructure of high temperature Ti-based brazing alloys and wettability on SiC ceramic

Interfacial Reaction and Brazing Behaviour of SiCf/SiC with Cf/C Composites Using Si-10Zr Alloy at High Temperatures

In Situ TiSi2 Microarray Reinforced Si–Ti Eutectic Colonies in Cf/C Composite Joints for High-Temperature Application

Microstructure and properties of different carbon fiber reinforced ceramic composites brazed joint by Si-Ti alloy filler

Microstructure and properties of an Al–Ti–Cu–Si brazing alloy for SiC–metal joining

Microstructure and Properties of C/C and C/SiC Composites Brazed by Reactive Infiltration of Si Zr Filler Alloy

Microstructure and properties of C/C and C/SiC composites brazed by reactive infiltration of SiZr filler alloy

Interfacial microstructure and mechanical properties of TiAl and C/SiC joint brazed with TiH2-Ni-B brazing powder

Brazing ZrB2-SiC Ceramics to Ti6Al4V Alloy with TiCu-based Amorphous Filler

Brazing of Ti-coated SiC Using a CoFeCrNiCu High Entropy Alloy Filler Via Electric Field-Assisted Sintering

Microstructural Evolution and Mechanical Properties of the Joint of TiAl Alloys and C/SiC Composites Vacuum Brazed with Ag–Cu Filler Metal

Microstructure Evolution and Mechanical Property of ZrC-SiC/Ti6Al4V Joints Brazed Using Ti-15Cu-15Ni Filler

Microstructure and properties of pressure-less joining of SiCf/SiC composites by Ti–Si alloys

Interfacial Microstructure and Mechanical Property of ZrC-SiC Ceramic and Ti6Al4V Joint Brazed with AgCuTi Alloy

Inducing Low-Temperature Melting of TiNiCuNb Eutectic Alloy for Manufacturing Strong C/C-SiC Composite Joints

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Achieving SiC Joints with Outstanding High-Temperature Property Via Flash Brazing Using FeCoCrNiCu High-Entropy Alloy