Preeminent Energy Storage Properties and Superior Stability of (Ba(1-X)bix)(ti(1-x)mg2x /3tax/3)o3 Relaxor Ferroelectric Ceramics Via Elongated Rod-Shaped Grains and Domain Structural Regulation

Ming Yin,Ying Zhang,Hai-Rui Bai,Peng Li,Yu-Chao Li,Wei-Fang Han,Ji-Gong Hao,Wei Li,Chun-Ming Wang,Peng Fu

DOI: https://doi.org/10.1016/j.jmst.2023.10.036

2024-01-01

Abstract:(Ba(1-x)Bix)(Ti(1-x)Mg2x/3Tax/3)O3 (BBTMT-x, x = 0.075, 0.1, 0.125, and 0.15) ceramics were manufactured via a solid-phase reaction method. The pseudo-cubic BaTiO3 (BT) as the primary phase and Ba4MgTi11 O27 as the secondary phase were detected in BBTMT-x ceramics. The elongated rod-shaped grains therein became numerous as x increased. The introduction of Bi/Mg/Ta (BMT) elements transformed BT ceramics from ferroelectrics to relaxor ferroelectrics and induced the formation of short-range order polar nanoregions (PNRs), which were beneficial for the preeminent energy storage properties (ESPs). The highest ESPs (a giant recoverable energy-storage density Wrec of 5.97 J cm-3 with a high-efficiency 77 of 87.4%) were achieved in BBTMT-0.1 ceramics at 710 kV cm-1. BBTMT-0.1 ceramics also possessed excellent frequency (1-500 Hz), temperature (30-150 degrees C), and fatigue (cycle number of 1-10 0,0 0 0) stabilities. Finite element simulations (FES) demonstrated that elongated rod-shaped grains had stronger obstacles to the development of electrical branches, which was beneficial to improving the comprehensive ESPs.(c) 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.