Realizing enhanced energy storage performances in (Bi0.5Na0.5)0.7Sr0.3TiO3-based relaxor ferroelectrics via components regulation

Fei Wang,Xu Li,Ning Chen,Zhi Tan,Shifa Wang,Jie Xing,Jianguo Zhu

DOI: https://doi.org/10.1016/j.ceramint.2022.06.184

IF: 5.532

2022-10-01

Ceramics International

Abstract:For (Na0.5Bi0.5)0.7Sr0.3TiO3-based relaxor ferroelectrics, the early polarization saturation and low breakdown electric field (E b) are considered critical bottlenecks. As a result, the further development of this kind of promising material is severely restricted. Along these lines, in this work, comprehensive energy storage performances were achieved by the Bi(Mg2/3Ta1/3)O3 modified (Bi0.5Na0.5)0.7Sr0.3TiO3 ceramics [abbreviated as (1-x)BNST-xBMT]. The restrained rapid polarization saturation and large difference in the polarization were observed by the domain relaxor behavior. The improved microstructures and decreased grain sizes further enhanced the E b values of BNST-based ceramics. Consequently, the suppressing premature saturation polarization, large polarization difference and high E b value synergistically contributed to the enhanced comprehensive energy storage performances [the recoverable energy density W rec of >3.0 J/cm3 and efficiency η of >85.0%]. Impressive stabilities of temperature (20 °C–200 °C) and frequency (1 Hz–200 Hz) were also demonstrated for the corresponding ceramics. Our results pave the way for improving the energy storage properties and further promoting the development of BNST-based ceramics.

materials science, ceramics