Achieving ultrahigh energy storage properties with superior stability in novel (Ba(1-)Bi )(Ti(1-)Zn0.5Sn0.5)O3 relaxor ferroelectric ceramics via chemical modification
Ming Yin,Guang-Jian Bai,Peng Li,Ji-Gong Hao,Wei Li,Wei-Fang Han,Yu-Chao Li,Chun-Ming Wang,Guo-Rong Li,Peng Fu
DOI: https://doi.org/10.1016/j.cej.2023.141724
IF: 15.1
2023-03-01
Chemical Engineering Journal
Abstract:Relaxor ferroelectrics are receiving widespread attention due to their excellent energy storage properties (ESPs). In this study, (Ba(1- x )Bi x )(Ti(1- x )Zn0.5 x Sn0.5 x )O3 (abbreviated as BBTZS-x, x = 0.08, 0.10, 0.12, 0.14, 0.16, 0.18) ceramics were synthesized via a solid-state reaction route, and the effects of chemical modification on their structure and properties were investigated in detail. The introduction of Bi/Zn/Sn (BZS) elements into BaTiO3 (BT) systems induced the change from normal to relaxor ferroelectric behavior, which caused the enhancement of comprehensive ESPs. Significantly, BBTZS-0.12 ceramics acquired the preeminent total energy density (W tot = 5.8 J/cm3), recoverable energy density (W rec = 4.99 J/cm3) and efficiency (η = 86.1%) at high field strength of 550 kV/cm because of the existence of polar nanoregions (PNRs) therein. The dynamic response of PNRs to the external field was found to be propitious to the enhancement of energy-storage performance. In particular, excellent current density (C D = 721.5 A/cm2), power density (P D = 151.5 MW/cm3) and the time of release of up to 90% of the discharge energy density value (t 0.9 = 53 ns) were simultaneously achieved in BBTZS-0.12 ceramics at 420 kV/cm. Moreover, BBTZS-0.12 ceramics were found to be the most optimal for the long-term applications under different environmental conditions because of their outstanding temperature (30–150 °C), frequency (1–500 Hz), and fatigue cycle (cycle numbers: 1–100000) stabilities. Therefore, exceptional ESPs make BBTZS-x ceramics promising for advanced pulsed power capacitors and energy storage applications.
engineering, chemical, environmental