Enhanced Energy Storage Performance And Thermal Stability In Relaxor Ferroelectric (1-X)Bifeo3-X(0.85batio(3)-0.15bi(Sn0.5zn0.5)O-3) Ceramics

Shuaishuai Ji,Qianjie Li,Dongdong Wang,Jiangyuan Zhu,Min Zeng,Zhipeng Hou,Zhen Fan,Xingsen Gao,Xubing Lu,Qiliang Li,Jun-Ming Liu

DOI: https://doi.org/10.1111/jace.17705

IF: 4.186

2021-01-01

Journal of the American Ceramic Society

Abstract:Lead-free (1-x)BiFeO3-x(0.85BaTiO(3)-0.15Bi(Sn0.5Zn0.5)O-3) [(1-x)BF-x(BT-BSZ), x=0.45-0.7] ceramic samples were prepared by solid phase sintering. It is revealed that the pure single-phase perovskite structure can be obtained in samples with x >= 0.6. With increasing x, the measured ferroelectric hysteresis loop becomes gradually slimmed in accompanying with reduced remnant polarization, and a clear ferroelectric-relaxor transition at x = 0.65 is identified. Furthermore, the measured electric breakdown strength can be significantly enhanced with increasing x, and the optimal energy storage performance is achieved at x = 0.65, characterized by the recoverable energy storage density up to approximate to 3.06 J/cm(3) and energy storage efficiency as high as approximate to 92 %. Excellent temperature stability (25 degrees C-110 degrees C) and fatigue endurance (>10(5) cycles) for energy storage are demonstrated. Our results suggest that the BF-based relaxor ceramics can be tailored for promising applications in high energy storage devices.