Simultaneously achieving high energy storage density and efficiency under low electric field in BiFeO3-based lead-free relaxor ferroelectric ceramics

Zhiteng Chen,Xingying Bu,Bingxin Ruan,Juan Du,Peng Zheng,Lili Li,Fei Wen,Wangfeng Bai,Wei Wu,Liang Zheng,Yang Zhang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.06.073
IF: 5.7
2020-12-01
Journal of the European Ceramic Society
Abstract:<p>BiFeO<sub>3</sub>-BaTiO<sub>3</sub>-based relaxor ferroelectric ceramic has attracted increasing attention for energy storage applications. However, simultaneously achieving high recoverable energy storage density (<em>W</em><sub>rec</sub>) and efficiency (<em>η</em>) under low electric field has been a longstanding drawback for their practical applications. Herein, a novel relaxor ferroelectric material was designed by introducing (Sr<sub>0.7</sub>Bi<sub>0.2</sub>)TiO<sub>3</sub> (SBT) into the composition 0.67BiFeO<sub>3</sub>-0.33BaTiO<sub>3</sub> (BF-BT-<em>x</em>SBT). A large <em>W</em><sub>rec</sub> of ∼2.40 J/cm<sup>3</sup> and a high <em>η</em> of ∼90.4 % were simultaneously realized under a low electric field of 180 kV/cm, which is superior to that of most previously reported lead-free ceramics. Moreover, moderate temperature endurance and excellent frequency stability were also obtained. More importantly, this ceramic has a large discharge current density (∼289.18 A/cm<sup>2</sup>), a discharge power density (∼14.46 MW/cm<sup>3</sup>) and short discharge time (&lt;0.25 μs). These results not only demonstrate superior potential in BF-BT-SBT ceramics, but also offer a new design to tune the energy storage performance of lead-free relaxor ferroelectric ceramics.</p>
materials science, ceramics
What problem does this paper attempt to address?