Enhanced energy storage performance and thermal stability in relaxor ferroelectric (1‐x)BiFeO 3 ‐x(0.85BaTiO 3 ‐0.15Bi(Sn 0.5 Zn 0.5 )O 3 ) ceramics

Shuaishuai Ji,Qianjie Li,Dongdong Wang,Jiangyuan Zhu,Min Zeng,Zhipeng Hou,Zhen Fan,Xingsen Gao,Xubing Lu,Qiliang Li,Jun‐Ming Liu

DOI: https://doi.org/10.1111/jace.17705

IF: 4.186

2021-02-16

Journal of the American Ceramic Society

Abstract:<p>Lead‐free (1‐<i>x</i>)BiFeO₃‐<i>x</i>(0.85BaTiO₃‐0.15Bi(Sn_0.5Zn_0.5)O₃) [(1‐<i>x</i>)BF‐<i>x</i>(BT‐BSZ), <i>x</i>=0.45‐0.7] ceramic samples were prepared by solid phase sintering. It is revealed that the pure single‐phase perovskite structure can be obtained in samples with <i>x</i> ≥ 0.6. With increasing <i>x</i>, the measured ferroelectric hysteresis loop becomes gradually slimmed in accompanying with reduced remnant polarization, and a clear ferroelectric‐relaxor transition at <i>x</i> = 0.65 is identified. Furthermore, the measured electric breakdown strength can be significantly enhanced with increasing <i>x</i>, and the optimal energy storage performance is achieved at <i>x</i> = 0.65, characterized by the recoverable energy storage density up to ≈ 3.06 J/cm³ and energy storage efficiency as high as ≈ 92 %. Excellent temperature stability (25 °C – 110 °C) and fatigue endurance (&gt;10⁵ cycles) for energy storage are demonstrated. Our results suggest that the BF‐based relaxor ceramics can be tailored for promising applications in high‐energy storage devices.</p>

materials science, ceramics