Enhanced Energy Storage and Fast Charge-Discharge Properties of (1-X) BaTiO3-xBi(Ni1/2Sn1/2)O-3 Relaxor Ferroelectric Ceramics

Feng Si,Bin Tang,Zixuan Fang,Hao Li,Shuren Zhang

DOI: https://doi.org/10.1016/j.ceramint.2019.05.323

IF: 5.532

2019-01-01

Ceramics International

Abstract:In this work, we designed novel lead-free relaxor ferroelectric ceramics of (1-x) BaTiO3-xBi(Ni1/2Sn1/2)O-3 (abbreviated as (1-x)BT-xBNS, with x = 0-0.20). With an increasing concentration of BNS, (1-x)BT-xBNS solid solutions displayed a phase transition from tetragonal symmetry to pseudocubic symmetry with highly diffusive and frequency-dependent relaxor ferroelectric behavior. Modified by BNS, (1-x)BT-xBNS ceramics yielded slim polarization-electric field (P-E) loops and improved energy-storage performances. The optimal energy storage properties can be achieved at x = 0.10, and samples showed a high recoverable energy density of 2.526 J/cm(3) and a remarkably high energy efficiency of 93.89% under 240 kV/cm simultaneously at ambient temperature, which represent enhancements by 925% and 286%, respectively, over pure BaTiO3. The energy storage characteristics of the 0.9BT-0.1BNS ceramic manifested good thermal stability ( - 55-150 degrees C) and frequency stability (10 Hz-1 kHz), with a variation in recoverable energy density of less than 10%. Meanwhile, the pulsed charging-discharging measurement showed that the 0.9BT-0.1BNS ceramic had a fast discharge period of 67 ns and a large power density of 19 MW/cm(3). Due to the outstanding characteristics, there is potential for this new and environmentally friendly BT-based ceramic to be used in high-power pulse capacitor applications.