Abstract:With the continuous growth in sustainable and renewable technologies, ceramic capacitors are emerging as a promising energy storage device. Lead-free (1-x)[(Na0.4K0.1Bi0.5)0.94Ba0.06TiO3]-xLa0.2Sr0.7TiO3 (0 ≤ x ≤ 0.40) ceramics were prepared using the solid-state reaction technique for obtaining relaxor characteristics with improved energy storage density, efficiency, and temperature stability of dielectric permittivity. A high recoverable energy density (Wr) ∼ 2.39 J/cm3 with a good efficiency (η) of ∼ 75.21% was obtained for x = 0.30 composition under 220 kV/cm applied field. The specimen x = 0.30 exhibited excellent fatigue resistance during 105 cycles and good temperature stability of energy storage characteristics (Wr > 0.87 J/cm3, η > 74%) in the temperature range of 25–180 °C under 100 kV/cm. In addition, the temperature range in which the dielectric permittivity variation was less than ±15% was very wide (204 °C (63–267 °C) and 275 °C (39–314 °C) for x = 0.30 and 0.20 specimens, respectively). Significant improvements in material performance were attributed to A-site engineering, which resulted in a mixture of P4bm and R3c polar nano regions (PNRs), leading to reduced hysteresis loss and temperature-stable dielectric permittivity. Additionally, the size of PNRs ranged between 3 and 6 nm, with the P4bm phase dominating in the x = 0.30 specimen, leading to a large maximum polarization under an applied electric field. Therefore, (1-x)[(Na0.4K0.1Bi0.5)0.94Ba0.06TiO3]-xLa0.2Sr0.7TiO3 relaxor ceramics are promising for high energy density materials and electronic applications requiring high permittivity stability over a wide temperature range.

High energy storage density and temperature-stable dielectric properties for (1-x)Bi0.38Na0.38Sr0.24TiO3-xBaSnO3 lead-free relaxor ceramics

Enhanced energy-storage properties and dielectric temperature stability of (Bi0·5Na0.5)0.84Sr0·16Ti1-(Y0·5Nb0.5) O3 lead-free ceramics

Broadening the Dielectric Stability Temperature Range of BNBST Relaxor Ferroelectric Ceramics by Rare Earth Ce Doping for Energy Storage

Enhanced dielectric temperature stability and energy-storage properties of (Y0.5Nb0.5)4+ co-doped (Bi0.5Na0.5)0.94Ba0.06TiO3 lead-free relaxor ceramics

SrTiO3‐modified Bi0.5Na0.47Li0.03Ti0.99Sn0.01O3 Relaxor Ferroelectric Ceramics with High Energy Storage Performance

Large energy storage properties of lead-free (1-x)(0.72Bi0.5Na0.5TiO3-0.28SrTiO3)-xBiAlO3 ceramics at broad temperature range

[(Bi0.50Na0.40K0.10)0.94Ba0.06]1-xLaxTi0.975Ta0.025O3 lead-free relaxor ceramics with high energy storage density and thermally stable dielectric properties

High-temperature energy storage performances in (1-x)(Na0.50Bi0.50TiO3)-xBaZrO3 lead-free relaxor ceramics

Enhanced energy storage performance in (1-x)Bi0.85Sm0.15FeO3-xCa0.5Sr0.5Ti0.9Zr0.1O3 relaxor ceramics

Enhanced Energy Storage and Temperature-Stable Dielectric Properties in (1-x)[(Na0.4K0.1Bi0.5)0.94Ba0.06TiO3]-xLa0.2Sr0.7TiO3 Lead-Free Relaxor Ceramics

Transformation of Ba0.7Sr0.3TiO3 from ferroelectrics to relaxor ferroelectrics by doping of Bi(Mg0.5Sn0.5) and realization of high energy storage

Achieving high energy storage density in BaTiO3- (Bi0.5Li0.5)(Ti0.5Sn0.5)O3 lead-free relaxor ferroelectric ceramics

Improved energy storage performance achieved in Na0.5Bi0.5TiO3-based ceramics with good thermal stability at low electric field

Energy storage performance of Na0.5Bi0.5TiO3-based relaxor ferroelectrics with wide temperature range

Enhanced energy storage properties and large electrostrictive effect of Bi0.35Na0.35Ba0.09Sr0.21Ti(1-)(Al0.5Nb0.5) O3 relaxor ceramics

Achieving ultrahigh energy storage properties with superior stability in novel (Ba(1-)Bi )(Ti(1-)Zn0.5Sn0.5)O3 relaxor ferroelectric ceramics via chemical modification

Enhanced temperature stable dielectric property and energy-storage performance of (1-x)(0.66Bi0.5Na0.5TiO3–0.34Sr0.7Bi0.2TiO3)– xK0.5Nd0.5TiO3 lead-free relaxor electroceramics

Realizing enhanced energy storage performances in (Bi0.5Na0.5)0.7Sr0.3TiO3-based relaxor ferroelectrics via components regulation

Effective improved energy storage performances of Na0.5Bi0.5TiO3-based relaxor ferroelectrics ceramics by A/B-sites co-doping

Enhancement of energy storage and hardness of (Na0.5Bi0.5)0.7Sr0.3TiO3-based relaxor ferroelectrics via introducing Ba(Mg1/3Nb2/3)O3

Structure, dielectric, and relaxor properties of BaTiO3-modified high-entropy (Bi0.2Na0.2K0.2Ba0.2Ca0.2)TiO3 ceramics for energy storage applications