[(Bi0.50Na0.40K0.10)0.94Ba0.06]1-xLaxTi0.975Ta0.025O3 lead-free relaxor ceramics with high energy storage density and thermally stable dielectric properties

Benben Yan,Huiqing Fan,Arun Kumar Yadav,Chao Wang,Zhinan Du,Mengyuan Li,Weijia Wang,Wenqiang Dong,Shuren Wang

DOI: https://doi.org/10.1007/s10853-020-05070-y

IF: 4.5

2020-07-20

Journal of Materials Science

Abstract:Dielectric ceramics for capacitors have attained significant attention in current time owing to their large power densities and fast charge/discharge rates. Lead-free [(Bi0.50Na0.40K0.10)0.94Ba0.06]1-xLaxTi0.975Ta0.025O3 (abbreviated as BNKBTT-100xLa) relaxor ceramics are prepared using mixed-oxide technique. All ceramics are revealed a pseudo-cubic structure using X-ray diffraction technique. The long-range order existing in BNKBTT-100xLa ceramics is found to reduce with increasing composition. As a result, a highly effective energy storage density (Wrec) ~ 1.558 J/cm3 and efficiency (η) ~ 88.46% is achieved in BNKBTT-2La ceramic. In addition, BNKBTT-2La composition is fatigue-free up to 105 cycles. Also, BNKBTT-4La ceramic exhibits a dielectric constant (ε') ~ 2281 near 150 °C with Δε'/ε'150 °C below 15% over a large range from 39 to 383 °C, showing an outstanding dielectric temperature stability. Therefore, BNKBTT-2La and BNKBTT-4La ceramics are outstanding for energy density and thermally stable dielectric permittivity, respectively, for the device applications.

materials science, multidisciplinary