High-temperature stability of dielectric and energy-storage properties of weakly-coupled relaxor (1-x)BaTiO3-xBi(Y1/3Ti1/2)O3 ceramics

Cuiying Ma,Huiling Du,Jia Liu,Le Kang,Xian Du,Xueyan Xi,Hongpei Ran

DOI: https://doi.org/10.1016/j.ceramint.2021.05.231

IF: 5.532

2021-06-01

Ceramics International

Abstract:<p>Lead-free (1-<em>x</em>)BaTiO₃-<em>x</em>Bi(Y_1/3Ti_1/2)O₃ ceramics (abbr. (1-<em>x</em>)BT-<em>x</em>BYT) were synthesized via a solid state process. X-ray diffraction (XRD) measurements and Raman spectra reveal that, for <em>x</em> ˃ 0.05, the ceramics structure changes from a ferroelectric tetragonal to a pseudo-cubic phase at room temperature. Dielectric tests indicate that the ceramics exhibit a relaxor behavior, the temperature (<em>T</em>_<em>m</em>) at which the maximum dielectric constant (<em>ε</em>_<em>m</em>) is obtained shifts towards lower values. As the BYT content increases, the dielectric dispersion factor (<em>γ</em>) increases from 0.99 to 1.86, the temperature coefficient of permittivity (<em>TC</em>_<em>ϵ</em>) decreases to ~60 ppm/°C, and the capacitance variation is within temperature coefficient of capacitance (TCC) ≤ 15% in the temperature range from RT to 400 °C (x = 0.20). Furthermore, as the BYT content increases, high polarization maxima (<em>P</em>_<em>max</em>), low remnant polarization (<em>P</em>_<em>r</em>), and slim <em>P-E</em> hysteresis loops can be observed. An energy storage density (<em>W</em>_<em>rec</em>) of 1.02 J/cm³ and energy efficiency (<em>η</em>) of 78% were achieved for <em>x</em> = 0.15, while these amounted to 0.77 J/cm³ and 90% for <em>x</em> = 0.2. Moreover, good temperature stability of energy storage properties is also obtained. These results indicate that the as-synthesized (1-<em>x</em>)BT-<em>x</em>BYT ceramics are potential lead-free materials for energy storage applications.</p>

materials science, ceramics