Microstructures and Formation Mechanism of Continuous Carbon Fiber-Reinforced (tizrhfnbta)c High-Entropy Ceramic Composites Fabricated Via High-Entropy Alloy Reactive Melt Infiltration

Haoran He,Jin'ge Yang,Wenjian Guo,Shifeng Zhang,Shuxin Bai

DOI: https://doi.org/10.1016/j.ceramint.2023.09.032

IF: 5.532

2023-01-01

Ceramics International

Abstract:Using TiZrHfNbTa high-entropy alloys as cation sources and carbon matrix in carbon fiber-reinforced carbon (C-f/C) preforms as carbon sources, this study presents rapid construction of dense, continuous C-f-reinforced (TiZrHfNbTa)C high-entropy ceramic (C-f/HEC) composites based on reactive melt infiltration (referred to as C-f/HECRMI composites). The results consistently indicate the uniform distribution of elements in the ceramic phase. Based on X-ray diffraction patterns, the ceramic phase was inferred as a (TiZrHfNbTa)C HEC phase. C-f/HECRMI composites can form because the TiZrHfNbTa high-entropy alloy reacts with the carbon matrix to form uniform ceramic monomers, which spontaneously assemble into the (TiZrHfNbTa)C HEC phase under high-temperature conditions. Owing to the dense microstructures, the high strength of the (TiZrHfNbTa)C phase, high strength and toughness of the residual TiZrHfNbTa alloy phase, and C-f reinforcement, C-f/HECRMI composites exhibit excellent mechanical properties with a bending strength of 584.2 MPa. These composites also possess outstanding ablation resistance, with linear and mass rates of 0.6 mu m s(-1) and 0.9 mg s(-1), respectively, under an ablation time of 180 s and ablation temperature maintained at similar to 2000 degrees C. The high ablation resistance can be attributed to dense, stable, and highly viscous complex oxides (HfZrO4, TiNbTaO7, Hf6Ta2O17, Nb2Zr6O17, ZrO2, and HfO2) formed on the sample surfaces.